Laboratory-based characterization of heteroepitaxial structures: Advanced experiments not needing synchrotron radiation

P. Zaumseil, A. Giussani, T. Schroeder

Powder Diffraction· Volume 25· Issue 2
Publisher page

Abstract

It is demonstrated that a complex X-ray characterization of semiconductor films epitaxially grown on metal oxide buffer layers and Si(111) substrates is possible using laboratory-based equipment. This is demonstrated with epi-germanium on Pr 2 O 3 as buffer material. Pole figure measurements prove that epi-Ge layers are nearly single crystalline with exactly the same in-plane orientation (type A) as the Si(111) substrate, while the lattice of the oxide layer is 180° rotated around the [111] surface normal (type B). Only a small fraction (less than 0.6 vol %) of the epi-Ge exhibits type B rotation twins. The main structural defects are microtwin lamellas lying in {111} planes 70.5° inclined to the wafer surface. The different in-plane orientation of the Si substrate and epi-Ge on one side and the Pr 2 O 3 buffer layer on the other side allows a very sensitive analysis of strain and defects even for a 10-nm oxide layer buried under a 100-nm Ge. The epi-Ge layers are nearly fully relaxed and the Pr 2 O 3 buffer layer is compressively strained. Due to the existing defects the Ge (111) planes are tilted in a characteristic pattern relative to the Si substrate.
Source: crossref · Quality: baseline

Research context

OpenAlex topics: Semiconductor materials and devices · Semiconductor materials and interfaces · Silicon Carbide Semiconductor Technologies

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (16)

Show source-provided references
1. IHP. (2009). RCREFSIMW, version 1.09 (simulation software) 〈www.ihp-microelectronics.com〉.
2. 10.4028/www.scientific.net/SSP.156-158.46710.4028/www.scientific.net/SSP.156-158.467 ↗
3. Waser · 2003
4. 10.1016/0022-0248(91)90687-Z10.1016/0022-0248(91)90687-Z ↗
5. 10.1063/1.306819810.1063/1.3068198 ↗
6. 10.1063/1.166386110.1063/1.1663861 ↗
7. 10.1016/j.mee.2007.04.01910.1016/j.mee.2007.04.019 ↗
8. 10.1088/1367-2630/10/11/11300410.1088/1367-2630/10/11/113004 ↗
9. 10.1016/j.jcrysgro.2008.08.06210.1016/j.jcrysgro.2008.08.062 ↗
10. 10.1063/1.33555110.1063/1.335551 ↗
11. 10.1016/j.mseb.2005.08.11310.1016/j.mseb.2005.08.113 ↗
12. 10.1063/1.287027010.1063/1.2870270 ↗
13. 10.1088/0022-3727/41/13/13530810.1088/0022-3727/41/13/135308 ↗
14. 10.1063/1.163771610.1063/1.1637716 ↗
15. 10.1088/0022-3727/32/10A/30410.1088/0022-3727/32/10A/304 ↗
16. 10.1063/1.296046510.1063/1.2960465 ↗