Direct evidence of mutual control of ferroelectric polarization and magnetization in Y-type hexaferrite BaSrCo2Fe12-Al O22 ceramics

Hexaferrites that exhibit the intrinsic and strong magnetoelectric (ME) coupling effect have been considered the most promising candidate for single-phase multiferroics. Currently, the strong ME coupling effect in this system was widely reported in single crystal form, while it is rare in polycrystalline one. In this work, Y-type hexaferrite BaSrCo ₂Fe _12-xAl _xO ₂₂ ( x = 0.0, 0.3, 0.6 and 0.9) ceramics were manufactured with conventional solid-state reaction. Their magnetic, dielectric, and ME coupling properties were systematically surveyed. It was revealed that Al doping could result in a high magnetic transition temperature of ~ 345 K for x = 0.9. Also, the ferroelectric polarization and abnormal magnetodielectric properties were significantly enhanced which could be maintained down to 200 K. Most interestingly, the sample x = 0.9 displayed strong direct and converse ME coefficients of ~ 400 ps/m and ~ 900 ps/m at 150 K, respectively. Therefore, these results reveal that Al doping can broaden our understanding of the Y-type hexaferrite in room-temperature multiferroics.