DataVXnpj Materials DegradationPaper
journal article·2021-05-20Open access

Influence of accessory phases and surrogate type on accelerated leaching of zirconolite wasteforms

Lewis R. Blackburn, Rachel Crawford, Samuel A. Walling, Laura J. Gardner, Max R. Cole, Shi-Kuan Sun, Clémence Gausse, Amber R. Mason, Martin C. Stennett, Ewan R. Maddrell, Neil C. Hyatt, Claire L. Corkhill

npj Materials Degradation· Volume 5· Issue 1
Publisher pageOpen full text
Source abstract

Abstract

Abstract A fraction of the UK Pu inventory may be immobilised in a zirconolite ceramic matrix prior to disposal. Two zirconolite compositions, targeting CaZr0.80Ce0.20Ti2O7 and CaZr0.80U0.20Ti2O7, were fabricated by hot isostatic pressing, alongside a reformulated composition, nominally Ca0.80Zr0.90Ce0.30Ti1.60Al0.40O7, with an excess of Ti and Zr added to preclude the formation of an accessory perovskite phase. Materials were subjected to accelerated leaching in a variety of acidic and alkaline media at 90 °C, over a cumulative period of 14 d. The greatest Ce release was measured from CaZr0.80Ce0.20Ti2.00O7 exposed to 1 M H2SO4, for which 14.7 ± 0.2% of the original Ce inventory was released from the wasteform into solution. The extent of Ce leaching into the solution was correlated with the quantity of perovskite present in the wasteform, and associated with the incorporation and preferential dissolution of Ce3+. CaZr0.80U0.20Ti2.00O7 exhibited improved leach resistance relative to CaZr0.80Ce0.20Ti2.00O7, attributed to the decreased proportion of accessory perovskite, with 7.1 ± 0.1% U released to in 8 M HNO3 after 7 d. The Ca0.80Zr0.90Ce0.30Ti1.60Al0.40O7 composition, with no accessory perovskite phase, presented significantly improved leaching characteristics, with < 0.4%Ce released in both 8 M HNO3 and 1 M H2SO4. These data demonstrate the need for careful compositional design for zirconolite wasteforms with regard to accessory phase formation and surrogate choice.
Source: crossref · Quality: baseline

Research context

Ceramics & glassesElectronic materials

OpenAlex topics: Nuclear materials and radiation effects · Radioactive element chemistry and processing · Ferroelectric and Piezoelectric Materials

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (33)

Show source-provided references
1. Hyatt, N. C. Safe management of the UK separated plutonium inventory: a challenge of materials degradation. npj Mater. Degrad. 4, 28 (2020).10.1038/s41529-020-00132-7 ↗
2. Gatehouse, B. M., Grey, I. E., Hill, R. J. & Rossell, H. J. Zirconolite, CaZrxTi3−xO7; Structure refinements for near-end-member compositions with x = 0.85 and 1.30. Acta Cryst. B37, 306–312 (1981).10.1107/S0567740881002914 ↗
3. Blackburn, L. R. et al. A systematic investigation of the phase assemblage and microstructure of the zirconolite CaZr1−xCexTi2O7 system. J. Nucl. Mater. 535, 152137 (2020).10.1016/j.jnucmat.2020.152137 ↗
4. Gilbert, M. R. et al. Synthesis and characterisation of Pu-doped zirconolites - (Ca1−xPux)Zr(Ti2−2xFe2x)O7. IOP Conf. Ser. Mater. Sci. Eng. 9, 012007 (2010).10.1088/1757-899X/9/1/012007 ↗
5. Ma, S. et al. Effects of ionic radius on phase evolution in Ln-Al co-doped Ca1−xLnxZrTi2−xAlxO7 (Ln = La, Nd, Gd, Ho, Yb) solid solutions. Ceram. Int. 44, 15124–15132 (2018).10.1016/j.ceramint.2018.05.149 ↗
6. Begg, B. D., Day, R. A. & Brownscombe, A. Structural Effect of Pu Substitutions on the Zr-site in Zirconolite. in Mat. Res. Soc. Symp. Proc. 663, 1–8 (2001).10.1557/PROC-663-259 ↗
7. Ewing, R. C., Weber, W. J. & Lian, J. nuclear waste disposal-pyrochlore (A2B2O7): Nuclear waste form for the immobilization of plutonium and ‘minor’ actinides. J. Appl. Phys. 95, 5949–5971 (2004).10.1063/1.1707213 ↗
8. Clinard, F. W. et al. Alpha decay self-irradiation damage in 238Pu-substituted zirconolite. J. Nucl. Mater. 105, 248–256 (1982).10.1016/0022-3115(82)90381-6 ↗
9. Begg, B. D., Vance, E. R., Day, R. A., Hambley, M. & Conradson, S. D. Plutonium and neptunium incorporation in zirconolite. Mater. Res. Soc. Symp. Proc. 465, 325–332 (1997).10.1557/PROC-465-325 ↗
10. Meng, C., Ding, X., Li, W., Zhao, J. & Yang, H. Phase structure evolution and chemical durability studies of Ce-doped zirconolite–pyrochlore synroc for radioactive waste storage. J. Mater. Sci. 51, 5207–5215 (2016).10.1007/s10853-016-9822-x ↗
11. Cai, X., Teng, Y., Wu, L., Zhang, K. & Huang, Y. The synthesis and chemical durability of Nd-doped single-phase zirconolite solid solutions. J. Nucl. Mater. 479, 455–460 (2016).10.1016/j.jnucmat.2016.07.042 ↗
12. Strachan, D. M. et al. Radiation damage effects in candidate titanates for Pu disposition: Zirconolite. J. Nucl. Mater. 372, 16–31 (2008).10.1016/j.jnucmat.2007.01.278 ↗
13. Icenhower, J. P. et al. Dissolution kinetics of pyrochlore ceramics for the disposition of plutonium. Am. Miner. 91, 39–53 (2006).10.2138/am.2006.1709 ↗
14. Smith, K. L., Lumpkin, G. R., Blackford, M. G., Day, R. A. & Hart, K. P. The durability of Synroc. J. Nucl. Mater. 190, 287–294 (1992).10.1016/0022-3115(92)90092-Y ↗
15. Vance, E. R. et al. Incorporation of uranium in Zirconolite (CaZrTi2O7). J. Am. Ceram. Soc. 85, 1853–1859 (2002).10.1111/j.1151-2916.2002.tb00364.x ↗
16. Zhang, Y. et al. Zirconolite-rich titanate ceramics for immobilisation of actinides - waste form/HIP can interactions and chemical durability. J. Nucl. Mater. 395, 69–74 (2009).10.1016/j.jnucmat.2009.09.019 ↗
17. Marples, J. A. C. The plutonium-zirconium phase diagram. J. Less Common. Met. 2, 331–351 (1960).10.1016/0022-5088(60)90042-4 ↗
18. Albiol, T., Serizawa, H. & Arai, Y. Studies in the PuO2-ZrO2 pseudo-binary phase diagram. J. Nucl. Sci. Technol. 3, 834–837 (2002).10.1080/00223131.2002.10875598 ↗
19. Vance, E. R. et al. In Environmental Issues and Waste Management Technologies in the Ceramic and Nuclear Industries IX .(eds. Vienna J. D. & Spearing D. R.) (Wiley, 2006).
20. Grey, I. E., Mumme, W. G., Ness, T. J., Roth, R. S. & Smith, K. L. Structural relations between weberite and zirconolite polytypes - Refinements of doped 3T and 4M Ca2Ta2O7 and 3T CaZrTi2O7. J. Solid State Chem. 174, 285–295 (2003).10.1016/S0022-4596(03)00222-6 ↗
21. Hubert, S., Heisbourg, G., Dacheux, N. & Moisy, P. Effect of inorganic ligands and hydrogen peroxide on ThO2 dissolution. Behavour of Th0.87Pu0.13O2 during leaching test. Inorg. Chem. 47, 2064–2073 (2008).10.1021/ic702065z ↗
22. Nesbitt, H. W. et al. Thermodynamic stability and kinetics of perovskite dissolution. Nature 289, 358–362 (1981).10.1038/289358a0 ↗
23. Myhra, S., Bishop, H. E., Rivière, J. C. & Stephenson, M. Hydrothermal dissolution of perovskite (CaTiO3). J. Mater. Sci. 22, 3217–3226 (1987).10.1007/BF01161185 ↗
24. Pham, D. K., Neall, F. B., Myhra, S., Smart, R. S. C. & Turner, P. S. Dissolution mechanisms of CaTiO3 - solution analysis, surface analysis and electron microscope studies – Implications for Synroc. Mat. Res. Soc. Symp. Proc. 127, 231–240 (1989).10.1557/PROC-127-231 ↗
25. Zhang, Z., Blackford, M. G., Lumpkin, G. R., Smith, K. L. & Vance, E. R. Aqueous dissolution of perovskite (CaTiO3): effects of surface damage and [Ca2+] in the leachant. J. Mater. Res. 20, 2462–2473 (2005).10.1557/jmr.2005.0294 ↗
26. Clark, B. M., Sundaram, S. K. & Misture, S. T. Polymorphic transitions in cerium-substituted zirconolite (CaZrTi2O7). Sci. Rep. 7, 2–10 (2017).10.1038/s41598-017-00046-6 ↗
27. Blackburn, L. R., Walling, S. A. & Hyatt, N. C. et al. Synthesis and characterisation of Ca1−xCexZrTi2−2xCr2xO7: analogue zirconolite wasteform for the immobilisation of stockpiled UK plutonium. J. Eur. Ceram. Soc. 40, 5909–5919 (2020).10.1016/j.jeurceramsoc.2020.05.066 ↗
28. Gardner, L. J., Walling, S. A. & Hyatt, N. C. Hot isostatic pressing: thermal treatment trials of inactive and radioactive simulant UK intermediate level waste. IOP Conf. Ser. Mater. Sci. Eng. 818, 012009 (2020).10.1088/1757-899X/818/1/012009 ↗
29. Hyatt, N. C. et al. The HADES Facility for High Activity Decommissioning Engineering & Science: part of the UK National Nuclear User Facility. IOP Conf. Ser. Mater. Sci. Eng. 818, 012022 (2020).10.1088/1757-899X/818/1/012022 ↗
30. Ravel, B. & Newville, M. ATHENA, ARTEMIS, HEPHAESTUS: Data analysis for X-ray absorption spectroscopy using IFEFFIT. J. Synchrotron Radiat. 12, 537–541 (2021).10.1107/S0909049505012719 ↗
31. ASTM International. Standard test methods for determining chemical durability of nuclear, hazardous, and mixed waste glasses and multiphase glass ceramics: The Product Consistency Test (PCT). https://doi.org/10.1520/C1285-14.2.10.1520/C1285-14.2 ↗
32. Parkhurst, D. L. & Appelo, C. A. J. Description of input and examples for PHREEQC Version 3—A Computer Program for Speciation, Batch-Reaction, One-Dimensional Transport, and Inverse Geochemical Calculations. Chapter 43 of Section A, in Groundwater Book 6, Modeling Techniques, Techniques and Methods 6-A43 (1999). https://pubs.usgs.gov/tm/06/a43/pdf/tm6-A43.pdf.
33. Brookins, D. G. Eh-pH diagrams for geochemistry. Geochim. Cosmochim. Acta 53, (1989).10.1007/978-3-642-73093-1 ↗