Room-Temperature Processing of TiOx Electron Transporting Layer for Perovskite Solar Cells
Source abstract
Abstract
In order to realize high-throughput roll-to-roll manufacturing of flexible perovskite solar cells, low-temperature processing of all device components must be realized. However, the most commonly used electron transporting layer in high-performance perovskite solar cells is based on TiO 2 thin films processed at high temperature (>450 °C). Here, we demonstrate room temperature solution processing of the TiO x layer that performs as well as the high temperature TiO 2 layer in perovskite solar cells, as evidenced by a champion solar cell efficiency of 16.3%. Using optical spectroscopy, electrical measurements, and X-ray diffraction, we show that the room-temperature processed TiO x is amorphous with organic residues, and yet its optical and electrical properties are on par with the high-temperature TiO 2 . Flexible perovskite solar cells that employ a room-temperature TiO x layer with a power conversion efficiency of 14.3% are demonstrated.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Perovskite Materials and Applications · Conducting polymers and applications · Chalcogenide Semiconductor Thin Films
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Chemical Engineering, University of Virginia, Charlottesville, Virginia 22904, United States
Department of Electrical and Computer Engineering, University of Virginia, Charlottesville, Virginia 22904, United States
NASA Langley Research Center, Hampton, Virginia 23681, United States
Funding
Langley Research Center · National Aeronautics and Space Administration
References (42)
Show source-provided references
1. NREL. ResearchCell Record Efficiency Chart http://www.nrel.gov/ncpv/images/efficiency_chart.jpg(accessed June 10th, 2017) .
2. 10.1039/C6EE01137C10.1039/C6EE01137C ↗
3. 10.1126/science.124398210.1126/science.1243982 ↗
4. 10.1039/C6NR09032J10.1039/C6NR09032J ↗
5. 10.1039/C5TA09520D10.1039/C5TA09520D ↗
6. 10.1016/j.nanoen.2017.03.04810.1016/j.nanoen.2017.03.048 ↗
7. 10.1039/C3EE43707H10.1039/C3EE43707H ↗
8. 10.1021/nl500399m10.1021/nl500399m ↗
9. 10.1021/nl403997a10.1021/nl403997a ↗
10. 10.1016/j.jpowsour.2014.12.10410.1016/j.jpowsour.2014.12.104 ↗
11. 10.1039/C6TA02105K10.1039/C6TA02105K ↗
12. 10.1038/nphoton.2013.34210.1038/nphoton.2013.342 ↗
13. 10.1038/ncomms841010.1038/ncomms8410 ↗
14. 10.1039/C5EE02155C10.1039/C5EE02155C ↗
15. 10.1246/cl.16116310.1246/cl.161163 ↗
16. 10.1088/0957-4484/28/1/01LT0210.1088/0957-4484/28/1/01LT02 ↗
17. 10.3390/mi802005510.3390/mi8020055 ↗
18. 10.1039/C5TA07515G10.1039/C5TA07515G ↗
19. 10.1002/adma.20130627110.1002/adma.201306271 ↗
20. 10.1039/C4EE02441A10.1039/C4EE02441A ↗
21. 10.1016/j.solmat.2017.02.00810.1016/j.solmat.2017.02.008 ↗
22. 10.1039/C4TA06416J10.1039/C4TA06416J ↗
23. 10.1039/C5MH00260E10.1039/C5MH00260E ↗
24. 10.1038/nphoton.2009.6910.1038/nphoton.2009.69 ↗
25. 10.1063/1.139859910.1063/1.1398599 ↗
26. 10.1038/nature1413310.1038/nature14133 ↗
27. 10.1038/nature1250910.1038/nature12509 ↗
28. 10.1126/sciadv.150117010.1126/sciadv.1501170 ↗
29. 10.1016/0022-3093(88)90007-510.1016/0022-3093(88)90007-5 ↗
30. 10.1021/cr00104a00310.1021/cr00104a003 ↗
31. 10.1002/adma.20070137210.1002/adma.200701372 ↗
32. 10.1126/science.114171110.1126/science.1141711 ↗
33. 10.1016/S0169-4332(01)00140-410.1016/S0169-4332(01)00140-4 ↗
34. 10.1016/j.jcrysgro.2005.05.03010.1016/j.jcrysgro.2005.05.030 ↗
35. 10.1103/PhysRevE.48.369210.1103/PhysRevE.48.3692 ↗
36. 10.1016/j.cplett.2012.12.01910.1016/j.cplett.2012.12.019 ↗
37. 10.1039/C4RA03630A10.1039/C4RA03630A ↗
38. 10.1155/2013/36547510.1155/2013/365475 ↗
39. 10.4028/www.scientific.net/KEM.602-603.103910.4028/www.scientific.net/KEM.602-603.1039 ↗
40. 10.1021/jz502471h10.1021/jz502471h ↗
41. 10.5923/j.ijee.20120203.0210.5923/j.ijee.20120203.02 ↗
42. 10.1016/S0040-6090(00)01015-410.1016/S0040-6090(00)01015-4 ↗