Hybrid Bismuth(III)-Halide Double Perovskite-Derived Ferroelastic (Pip)₂[KBiBr₆] with Excitonic and Bi(III) Luminescence due to Electronic Confinement along Inorganic Pillars

High Resolution Image Download MS PowerPoint Slide Organic–inorganic halide double perovskites with the A 2 MM′X 6 composition are considered a more stable and environmentally friendly alternative to lead-based APbX 3 compounds (3D HOIPs). Herein, we report the synthesis, crystal structure, physicochemical characterization, and the results of density functional theory (DFT) calculations for a double-perovskite-related (piperidinium) 2 [KBiBr 6 ]. Inorganic structure is built of 1D inorganic pillars composed of Bi(III)Br 6 octahedra face shared with trigonal KBr 6 antiprisms. It undergoes a room-temperature order–disorder phase transition at T c = 300/303 K (cooling/heating), associated with molecular dynamics and formation of stable hydrogen-bond interactions. Dielectric relaxation in the vicinity of T c indicates gradual ordering of piperidinium. The C 2/ m to P 1 − symmetry reduction leads to the formation of a switchable ferroelastic domain structure. The material shows purplish-blue photoluminescence from high-energy excitons and Bi(III) emission due to the electronic confinement along the inorganic pillars. DFT calculations of the density of states confirm that the electronic properties are governed by the electronic states of Bi(III)Br 6 octahedra and reveal that electron and hole migration occur between neighboring chains, being quenched along the inorganic part. The optical band gap E g is 2.8 eV.