First 14-Layer Twinned Hexagonal Perovskite Ba14Mn1.75Ta10.5O42: Atomic-Scale Imaging of Cation Ordering

Fengqiong Tao, Cécile Genevois, Fengqi Lu, Xiaojun Kuang, Florence Porcher, Liangju Li, Tao Yang, Wenbo Li, Di Zhou, Mathieu Allix

Chemistry of Materials· Volume 28· Issue 13

Abstract

Formation of hexagonal perovskite with mixed cubic and hexagonal stacking of AO 3 layers becomes more and more difficult when the number of layers in the stacking repeating unit increases. So far, the highest number of layers reported for twinned hexagonal perovskite is 12, with alternative 5 consecutive cubic layers and one hexagonal layer in the ( ccccch ) 2 sequence. Here, we present the unexpected formation of a 14-layer twinned hexagonal perovskite with a stacking sequence ( cccccch ) 2 for the BaO 3 layers on the Ba 14 Mn 1.75 Ta 10.5 O 42 (Ba 8 MnTa 6 O 24 ) composition, the first example of twinned hexagonal perovskite with a periodicity exceeding 12-layers. The B-cation and vacancy distributions are characterized by multiple efficient and complementary techniques including neutron and synchrotron powder diffraction, scanning transmission electron microscopy-high angle annular dark field (STEM-HAADF) imaging, and electron energy loss spectroscopy (EELS) and X-ray energy dispersive spectroscopy (EDS) elemental mapping. Atomic-resolution STEM-HAADF imaging and EELS/EDS elemental mapping enables direct observation of high-spin d 5 Mn 2+ cation ordering in the d 0 Ta 5+ host, thus demonstrating the great potential of this technique for probing cation ordering and performing structure determination. Moreover, atomic mapping allows for the observation of local defect structure variants, which can be a powerful tool for future new material design. The large high-spin Mn 2+ cation and Ta-vacancy pair formation in face-sharing octahedral sites play key roles on both the stabilization of this 14-layer twinned hexagonal perovskite structure and the Mn 2+ ordering in the central corner-sharing octahedral (CSO) positions within the five-consecutive CSO layers. Compared with the 8-layer twinned Ba 8 ZnTa 6 O 24 material, the low quality factor in microwave frequency and enhanced ultraviolet and visible light absorption of Ba 14 Mn 1.75 Ta 10.5 O 42 as well as the photocatalytic activity on water splitting are discussed in terms of the presence of high-spin Mn 2+ cations in the structure.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Microwave Dielectric Ceramics Synthesis · Ferroelectric and Piezoelectric Materials · Multiferroics and related materials

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Guangxi Ministry-Province Jointly-Constructed Cultivation Base for State Key Laboratory of Processing for Nonferrous Metal and Featured Materials, Guangxi Universities Key Laboratory of Non-ferrous Metal Oxide Electronic Functional Materials and Devices, College of Materials Science and Engineering, Guilin University of Technology, Guilin 541004, P. R. China

UPR3079 CEMHTI, 1D Avenue de la Recherche Scientifique, 45071 Orléans Cedex 2, France

Université d’Orléans, Faculté des Sciences, Avenue du Parc Floral, 45067 Orléans Cedex 2, France

CEA Saclay, Laboratoire Léon Brillouin, F-91191 Gif Sur Yvette, France

College of Chemistry and Chemical Engineering, Chongqing University, Chongqing 400044, P. R. China

Electronic Materials Research Laboratory, Key Laboratory of the Ministry of Education & International Center for Dielectric Research, Xi’an Jiaotong University, Xi’an 710049 Shaanxi, P. R. China

Funding

Centre National de la Recherche Scientifique · National Natural Science Foundation of China · Guangxi Key Laboratory for Advanced Materials and New Preparation Technology, Guilin University of Technology · Guangxi Province

References (37)

Show source-provided references
1. Rao C. N. R. · 1998
2. 10.1002/anie.20120488410.1002/anie.201204884 ↗
3. 10.1007/BF0130370110.1007/BF01303701 ↗
4. 10.1021/ja00088a01610.1021/ja00088a016 ↗
5. 10.1038/nmat378210.1038/nmat3782 ↗
6. 10.1111/j.1551-2916.2006.01025.x10.1111/j.1551-2916.2006.01025.x ↗
7. 10.1016/S1359-0286(00)00002-410.1016/S1359-0286(00)00002-4 ↗
8. 10.1016/j.jssc.2003.10.02410.1016/j.jssc.2003.10.024 ↗
9. 10.1111/j.1551-2916.2005.00426.x10.1111/j.1551-2916.2005.00426.x ↗
10. 10.1143/JJAP.45.749410.1143/JJAP.45.7494 ↗
11. 10.1021/cm202594410.1021/cm2025944 ↗
12. 10.1016/0022-4596(74)90005-X10.1016/0022-4596(74)90005-X ↗
13. 10.1111/j.1551-2916.2009.03548.x10.1111/j.1551-2916.2009.03548.x ↗
14. Coelho, A. A.Topas Academic V4;Coelho Software:Brisbane, Australia, 2005.
15. 10.1107/S010876818500206310.1107/S0108768185002063 ↗
16. 10.1063/1.158236310.1063/1.1582363 ↗
17. 10.1006/jssc.1996.027010.1006/jssc.1996.0270 ↗
18. 10.1039/C5DT00859J10.1039/C5DT00859J ↗
19. 10.1002/anie.20050013510.1002/anie.200500135 ↗
20. 10.1021/nl503077y10.1021/nl503077y ↗
21. 10.1002/adma.20080272810.1002/adma.200802728 ↗
22. 10.1146/annurev.matsci.37.052506.08435610.1146/annurev.matsci.37.052506.084356 ↗
23. 10.1103/PhysRevB.73.10440810.1103/PhysRevB.73.104408 ↗
24. 10.1107/S010876810302666110.1107/S0108768103026661 ↗
25. 10.1021/cm049831k10.1021/cm049831k ↗
26. 10.1107/S056773947600155110.1107/S0567739476001551 ↗
27. 10.1021/cm061647710.1021/cm0616477 ↗
28. 10.1080/0015019830824466610.1080/00150198308244666 ↗
29. 10.1103/PhysRevB.90.22440210.1103/PhysRevB.90.224402 ↗
30. 10.1016/S0025-5408(97)00034-210.1016/S0025-5408(97)00034-2 ↗
31. 10.1111/j.1551-2916.2005.00458.x10.1111/j.1551-2916.2005.00458.x ↗
32. 10.1016/j.matchemphys.2015.03.05710.1016/j.matchemphys.2015.03.057 ↗
33. 10.1016/j.commatsci.2013.07.04410.1016/j.commatsci.2013.07.044 ↗
34. 10.1021/cm702420310.1021/cm7024203 ↗
35. 10.1039/c3cs60438a10.1039/c3cs60438a ↗
36. 10.1002/adfm.20050084910.1002/adfm.200500849 ↗
37. 10.1246/cl.2005.82210.1246/cl.2005.822 ↗