Defective Ni Perovskites as Cathode Materials in Intermediate-Temperature Solid-Oxide Fuel Cells: A Structure−Properties Correlation
Source abstract
Abstract
Four oxides belonging to the perovskite series of nominal stoichiometry LaNi 1− x Mo x O 3, x = 0.10, 0.15, 0.20, 0.25 (LNMO), have been tested as cathode materials for solid oxide fuel cells (SOFC). The electrodes were supported on a 300-μm-thick pellet of the electrolyte La 0.8 Sr 0.2 Ga 0.83 Mg 0.17 O 3−δ (LSGM) with Sr 2 MgMoO 6 (SMMO) as the anode and LNMO as the cathode. The test fuel cells gave a maximum power density of 660 mW/cm 2 at 850 °C and 565 mW/cm 2 at 800 °C for the x = 0.25 cathode material and exhibited high cyclability and low cathodic overpotential losses with pure H 2 as fuel. All the cathode materials were characterized by X-ray diffraction (XRD) and electrical conductivity measurements while the test fuel cell cross-section was examined by scanning electron microscopy (SEM). The X-ray data indicate that all the cathode materials exhibit a perovskite phase with an additional impurity phase present in LNMO x = 0.20, 0.25 materials. Molybdenum (Mo)-poor LNMO x = 0.10 exhibits a purely metallic behavior in the 120−800 °C temperature range, while Mo-rich LNMO, x = 0.15, 0.20, and 0.25, are semiconducting. Additionally, analysis of in situ temperature-dependent neutron powder diffraction (NPD) data from LNMO x = 0.20 at 25 and 800 °C in air reveal that it possesses a rhombohedral structure ( R 3 c̅ space group) with a crystallographic formula La 0.98(1) Ni 0.88(3) Mo 0.12(3) O 2.78(3) and a nominal oxidation state for Ni of 2.16+, which points to the presence of a Ni(III)/Ni(II) redox couple in the cathode materials at the working temperature of the cell (800 °C). The Ni(III)/Ni(II) redox energy at the top of the O 2p bands accounts for a good electronic conductivity of polaronic nature of approximately 30 S·cm −1 at 800 °C. NPD data also showed a measurable oxygen deficiency of approximately 0.2 oxygen atoms per formula unit exhibiting large thermal factors, which accounts for the good oxygen mobility expected in a mixed ion−electronic conductor (MIEC) oxide. The excellent properties of LaNi 1− x Mo x O 3−δ cathodes, especially for x = 0.25, with long-term stability and low cathodic overpotential losses make them potential electrode materials for the first generation of cobalt-free intermediate-temperature SOFCs, with power densities exceeding the target of 500 mW/cm 2 at 800 °C in pure H 2 as a fuel.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Advancements in Solid Oxide Fuel Cells · Magnetic and transport properties of perovskites and related materials · Electronic and Structural Properties of Oxides
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Engineering Research Center of Nano-Geo Materials of Ministry of Education, China University of Geosciences, Wuhan, 430074, China.
Materials Science & Engineering Program, The University of Texas at Austin, Austin, Texas, 78712
Instituto de Ciencia de Materiales de Madrid, CSIC, Cantoblanco, E-28049 Madrid, Spain
Institute Laue-Langevin (ILL) 156X, F-38042 Grenoble Cedex 9, France
References (26)
Show source-provided references
1. Huang K. · 2009
2. Guo W. M. · J. Alloys Compd. · 2009 · 473 · 4310.1016/j.jallcom.2008.05.058 ↗
3. Lin Y. · Solid State Ionics · 2008 · 179 · 42010.1016/j.ssi.2008.02.063 ↗
4. Bidrawn F. · J. Electrochem. Soc. · 2008 · 155 · B66010.1149/1.2907431 ↗
5. Hsu M. F. · Electrochem. Solid State Lett. · 2006 · 9 · A19310.1149/1.2167929 ↗
6. Huang K. Q. · J. Electrochem. Soc. · 1997 · 114 · 362010.1149/1.1838058 ↗
7. Tai L.-W. · Solid State Ionics · 1995 · 76 · 27310.1016/0167-2738(94)00245-N ↗
8. Tai L.-W. · J. Solid State Chem. · 1995 · 118 · 11710.1006/jssc.1995.1319 ↗
9. Rietveld H. M. · J. Appl. Crystallogr. · 1969 · 2 · 6510.1107/S0021889869006558 ↗
10. Rodríguez-Carvajal J. · Physica B · 1993 · 192 · 5510.1016/0921-4526(93)90108-I ↗
11. Huang Y.-H. · Science · 2006 · 312 · 25410.1126/science.1125877 ↗
12. Rodriguez E. · J. Mater. Chem. · 2001 · 11 · 67310.1039/b005364n ↗
13. Xue J. S. · Chem. Mater. · 1995 · 7 · 33310.1021/cm00050a015 ↗
14. Touloukian Y. S. · 1977 · 13
15. Tarancón A. · J. Power Sources · 2007 · 174 · 25510.1016/j.jpowsour.2007.08.077 ↗
16. Goodenough J. B. · J. Appl. Phys. · 1965 · 36 · 103110.1063/1.1714087 ↗
17. Tiwari A. · J. Phys.: Condens. Matter · 1999 · 11 · 3291
18. Sreedhar K. · J. Solid State Chem. · 1994 · 110 · 20810.1006/jssc.1994.1161 ↗
19. Skinner S. J. · Mater. Today · 2003 · 6 · 3010.1016/S1369-7021(03)00332-8 ↗
20. Zhang Z. · J. Solid State Chem. · 1995 · 117 · 23610.1006/jssc.1995.1269 ↗
21. Alonso J. A. · J. Chem. Soc., Dalton Trans. · 1995 · 281910.1039/DT9950002819 ↗
22. Naiqing Z. · J. Rare Earths · 2006 · 24 · 9010.1016/S1002-0721(07)60331-7 ↗
23. Lee D. · J. Power Sources · 2007 · 166 · 3510.1016/j.jpowsour.2006.12.099 ↗
24. Brese N. E. · Acta Crystallogr., Sect. B · 1991 · 47 · 19210.1107/S0108768190011041 ↗
25. Brown I. D. · Z. Kristallogr. · 1992 · 199 · 25510.1524/zkri.1992.199.3-4.255 ↗
26. Shannon R. D. · Acta Crystallogr. · 1976 · 32 · 75110.1107/S0567739476001551 ↗