Atomic Layer Deposition of Gd2O3 and Dy2O3: A Study of the ALD Characteristics and Structural and Electrical Properties
Source abstract
Abstract
Gd 2 O 3 and Dy 2 O 3 thin films were grown by atomic layer deposition (ALD) on Si(100) substrates using the homoleptic rare earth guanidinate based precursors, namely, tris( N, N ′-diisopropyl-2-dimethylamido-guanidinato)gadolinium(III) [Gd(DPDMG) 3 ] ( 1 ) and tris( N, N ′-diisopropyl-2-dimethylamido-guanidinato)dysprosium(III) [Dy(DPDMG) 3 ] ( 2 ), respectively. Both complexes are volatile and exhibit high reactivity and good thermal stability, which are ideal characteristics of a good ALD precursor. Thin Gd 2 O 3 and Dy 2 O 3 layers were grown by ALD, where the precursors were used in combination with water as a reactant at reduced pressure at the substrate temperature ranging from 150 °C to 350 °C. A constant growth per cycle (GPC) of 1.1 Å was obtained at deposition temperatures between 175 and 275 °C for Gd 2 O 3, and in the case of Dy 2 O 3, a GPC of 1.0 Å was obtained at 200–275 °C. The self-limiting ALD growth characteristics and the saturation behavior of the precursors were confirmed at substrate temperatures of 225 and 250 °C within the ALD window for both Gd 2 O 3 and Dy 2 O 3 . Thin films were structurally characterized by grazing incidence X-ray diffraction (GI-XRD), atomic force microscopy (AFM), and transmission electron microscopy (TEM) analyses for crystallinity and morphology. The chemical composition of the layer was examined by Rutherford backscattering (RBS) analysis and Auger electron spectroscopy (AES) depth profile measurements. The electrical properties of the ALD grown layers were analyzed by capacitance–voltage ( C – V ) and current–voltage ( I – V ) measurements. Upon subjection to a forming gas treatment, the ALD grown layers show promising dielectric behavior, with no hysteresis and reduced interface trap densities, thus revealing the potential of these layers as high- k oxide for application in complementary metal oxide semiconductor based devices.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Semiconductor materials and devices · Electronic and Structural Properties of Oxides · ZnO doping and properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Inorganic Materials Chemistry, Ruhr-University Bochum, 44780 Bochum, Germany
Institute of Electronic Materials and Devices, Leibniz University of Hannover, 30167 Hannover, Germany
Center of Advanced European Studies and Research (Caesar), 53175 Bonn, Germany
Institute of Electronic Materials and Nanoelectronics, Ruhr-University Bochum, 44780 Bochum, Germany
Dynamitron Tandem Laboratory (DTL) of RUBION, Ruhr-University Bochum, 44780 Bochum, Germany
References (36)
Show source-provided references
1. Buenzil J. C. G. · Chem. Soc. Rev. · 2005 · 34 · 104810.1039/b406082m ↗
2. Kido J. · Chem. Rev. · 2002 · 102 · 235710.1021/cr010448y ↗
3. Robertson J. · Eur. Phys. J. Appl. Phys. · 2004 · 28 · 235710.1051/epjap:2004206 ↗
4. Gasgnier M. J. · Mater. Sci. · 1991 · 26 · 198910.1007/BF00549157 ↗
5. International Technology Roadmap for Semiconductors, 2010; available online:http://www.itrs.net/Links/2010ITRS/Home2010.htm.
6. Wilk G. D. · J. Appl. Phys. · 2001 · 89 · 524310.1063/1.1361065 ↗
7. Laha A. · Appl. Phys. Lett. · 2006 · 89 · 14351410.1063/1.2360209 ↗
8. Adelmann C. · J. Electrochem. Soc. · 2010 · 157 · G10510.1149/1.3301663 ↗
9. Govindarajan S. · Appl. Phys. Lett. · 2007 · 91 · 06290610.1063/1.2768002 ↗
10. Wiemer C. · Appl. Phys. Lett. · 2010 · 96 · 18290110.1063/1.3400213 ↗
11. Wagner M. · Appl. Phys. Lett. · 2006 · 88 · 17290110.1063/1.2198103 ↗
12. Myllymäki P. · Appl. Phys. A: Mater. Sci. Process. · 2007 · 88 · 63310.1007/s00339-007-4069-7 ↗
13. Van Elshocht S. · J. Electrochem. Soc. · 2006 · 153 · F21910.1149/1.2220076 ↗
14. Thomas R. · Appl. Phys. Lett. · 2006 · 89 · 23290210.1063/1.2402121 ↗
15. Thomas R. · Solid State Commun. · 2008 · 147 · 33210.1016/j.ssc.2008.05.014 ↗
16. Bera M. K. · Semicond. Sci. Technol. · 2010 · 25 · 06500810.1088/0268-1242/25/6/065008 ↗
17. Lee K. S. · J. Alloys Compd. · 2010 · 507 · 44810.1016/j.jallcom.2010.07.196 ↗
18. Chu L. K. · Appl. Phys. Lett. · 2009 · 94 · 20210810.1063/1.3139772 ↗
19. Osten H. J. · Phys. Status Solidi A · 2008 · 205 · 69510.1002/pssa.200723509 ↗
20. Leskelä M. · Angew. Chem. · 2003 · 42 · 554810.1002/anie.200301652 ↗
21. George S. M. · Chem. Rev. · 2010 · 110 · 11110.1021/cr900056b ↗
22. Niinistö J. · J. Cryst. Growth · 2005 · 285 · 19110.1016/j.jcrysgro.2005.08.002 ↗
23. Kukli K. · Chem. Vap. Deposition · 2007 · 13 · 54610.1002/cvde.200706631 ↗
24. Myllymäki P. · J. Mater. Chem. · 2010 · 20 · 420710.1039/c0jm00363h ↗
25. Milanov A. P. · Chem. Mater. · 2009 · 21 · 544310.1021/cm902123m ↗
26. Thiede T. B. · Chem. Mater. · 2011 · 23 · 143010.1021/cm102840v ↗
27. Milanov A. P. · Inorg. Chem. · 2008 · 47 · 1140510.1021/ic801432b ↗
28. Milanov A. P. · J. Am. Chem. Soc. · 2010 · 132 · 3610.1021/ja909102j ↗
29. Kótai E. · Nucl. Instrum. Methods · 1994 · 85 · 58810.1016/0168-583X(94)95888-2 ↗
30. Suntola T. · Mater. Sci. Rep. · 1989 · 4 · 26110.1016/S0920-2307(89)80006-4 ↗
31. Päiväsaari J. · Top. Appl. Phys. · 2007 · 106 · 1510.1007/11499893_2 ↗
32. Matero R. · Thin Solid Films · 2000 · 368 · 110.1016/S0040-6090(00)00890-7 ↗
33. Putkonen M. · Chem. Mater. · 2001 · 13 · 470110.1021/cm011138z ↗
34. Briggs D. · 1990
35. Schroder D. K. · 1990
36. Sun Q. Q. · Appl. Phys. Lett. · 2008 · 92 · 15290810.1063/1.2912523 ↗