Establishing Efficient Cobalt-Based Catalytic Sites for Oxygen Evolution on a Ta₃N₅ Photocatalyst

In a photocatalytic suspension system with a powder semiconductor, the interface between the photocatalyst semiconductor and catalyst should be constructed to minimize resistance for charge transfer of excited carriers. This study demonstrates an in-depth understanding of pretreatment effects on the photocatalytic O 2 evolution reaction (OER) activity of visible-light-responsive Ta 3 N 5 decorated with CoO x nanoparticles. The CoO x /Ta 3 N 5 sample was synthesized by impregnation followed by sequential heat treatments under NH 3 flow and air flow at various temperatures. Various characterization techniques, including X-ray diffraction (XRD), X-ray absorption spectroscopy (XAS), scanning transmission electron microscopy (STEM), and X-ray photoelectron spectroscopy (XPS), were used to clarify the state and role of cobalt. No improvement in photocatalytic activity for OER over the bare Ta 3 N 5 was observed for the as-impregnated CoO x /Ta 3 N 5, likely because of insufficient contact between CoO x and Ta 3 N 5 . When the sample was treated in NH 3 at high temperature, a substantial improvement in the photocatalytic activity was observed. After NH 3 treatment at 700 °C, the Co 0 –CoO x core–shell agglomerated cobalt structure was identified by XAS and STEM. No metallic cobalt species was evident after the photocatalytic OER, indicating that the metallic cobalt itself is not essential for the reaction. Accordingly, mild oxidation (200 °C) of the NH 3 -treated CoO x /Ta 3 N 5 sample enhanced photocatalytic OER activity. Oxidation at higher temperatures drastically eliminated the photocatalytic activity, most likely because of unfavorable Ta 3 N 5 oxidation. These results suggest that the intimate contact between cobalt species and Ta 3 N 5 facilitated at high temperature is beneficial to enhancing hole transport and that the cobalt oxide provides electrocatalytic sites for OER.