Preparation of Nanosized Perovskites and Spinels through a Silica Xerogel Template Route
Source abstract
Abstract
Aggregates of nanosized perovskites and spinels (particle sizes below 15 nm) have been prepared by means of a low-cost silica xerogel template route. High values of surface area for the perovskites and spinels are obtained.
Only a short abstract or summary was supplied by the source.
Source: openalex_inverted_index · Quality: short
Research context
OpenAlex topics: Mesoporous Materials and Catalysis · Catalytic Processes in Materials Science · Catalysis and Oxidation Reactions
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Instituto Nacional del Carbón (CSIC), c/Francisco Pintado Fe, 26, 33011 Oviedo, Spain
References (40)
Show source-provided references
1. Tejuca L. G. · Adv. Catal. · 1989 · 36 · 23710.1016/S0360-0564(08)60019-X ↗
2. Mehandjiev D. · Appl. Catal., A · 2001 · 206 · 1310.1016/S0926-860X(00)00570-6 ↗
3. Jansson J. · J. Catal. · 2002 · 211 · 38710.1016/S0021-9517(02)93738-3 ↗
4. Sekizawa K. · Appl. Catal., A · 1998 · 169 · 29110.1016/S0926-860X(98)00018-0 ↗
5. Tanaka Y. · Appl. Catal., A · 2003 · 242 · 28710.1016/S0926-860X(02)00529-X ↗
6. Sloczynski J. · Appl. Catal., B · 2000 · 24 · 4510.1016/S0926-3373(99)00093-4 ↗
7. Chen L. · Catal. Lett. · 1999 · 60 · 23710.1023/A:1019023527676 ↗
8. Sloczynski J. · J. Catal. · 1999 · 187 · 41010.1006/jcat.1999.2626 ↗
9. Singh J. P. · J. New Mater. Electrochem. Syst. · 2000 · 3 · 137
10. Tanaka Y. · J. Catal. · 2003 · 215 · 27110.1016/S0021-9517(03)00024-1 ↗
11. Pudmich G. · Solid State Ion · 2000 · 135 · 43310.1016/S0167-2738(00)00391-X ↗
12. Fergus J. W. · Solid State Ion · 2004 · 171 · 110.1016/j.ssi.2004.04.010 ↗
13. Huang X. · J. Alloy Compd. · 2002 · 345 · 26510.1016/S0925-8388(02)00411-5 ↗
14. Alcock C. B. · Solid State Ion · 1992 · 51 · 28110.1016/0167-2738(92)90210-G ↗
15. Shui J. L. · Electrochim. Acta · 2004 · 49 · 220910.1016/j.electacta.2004.01.002 ↗
16. Horiba T. · J. Power Sources · 2003 · 119 · 89310.1016/S0378-7753(03)00202-7 ↗
17. Kang E. · J. Phys. Chem. B · 2004 · 108 · 1393210.1021/jp049041y ↗
18. Manova E. · Chem. Mater. · 2004 · 16 · 568910.1021/cm049189u ↗
19. Landau M. V. · 2002 · 1765
20. Weidenkaff A. · Adv. Eng. Mater. · 2004 · 6 · 70910.1002/adem.200400098 ↗
21. Schüth F. · Angew. Chem., Int. Ed. · 2003 · 42 · 360410.1002/anie.200300593 ↗
22. Schwickardi M. · Chem. Mater. · 2002 · 14 · 391310.1021/cm0211857 ↗
23. Wakayama H. · Chem. Mater. · 2001 · 13 · 239210.1021/cm001408y ↗
24. Li W. C. · Chem. Mater. · 2004 · 16 · 567610.1021/cm048759n ↗
25. Roggenbuck J. · J. Am. Chem. Soc. · 2005 · 127 · 109610.1021/ja043605u ↗
26. Kang M. · Catal. Today · 2004 · 93 · 69510.1016/j.cattod.2004.06.063 ↗
27. Tian B. · Adv. Mater. · 2003 · 15 · 137010.1002/adma.200305211 ↗
28. Dong A. · J. Am. Chem. Soc. · 2003 · 125 · 497610.1021/ja029964b ↗
29. Laha S. C. · Chem. Commun. · 2003 · 213810.1039/B305524H ↗
30. Tian B. Z. · J. Am. Chem. Soc. · 2004 · 126 · 86510.1021/ja037877t ↗
31. Fuertes A. B. · J. Phys. Chem. Solids · 2005 · 66 · 74110.1016/j.jpcs.2004.09.010 ↗
32. Zhu K. K. · Chem. Commun. · 2003 · 9810.1039/b210065g ↗
33. Yang H. F. · J. Am. Chem. Soc. · 2003 · 125 · 472410.1021/ja034005i ↗
34. Lee K. · J. Am. Chem. Soc. · 2003 · 125 · 684410.1021/ja034137b ↗
35. Wang Y. · Adv. Mater. · 2005 · 17 · 5310.1002/adma.200400777 ↗
36. Fuertes A. B. · Chem. Mater. · 2004 · 16 · 44910.1021/cm0349405 ↗
37. Marbán G. · Appl. Catal., B · 2005 · 57 · 5310.1016/j.apcatb.2004.10.011 ↗
38. Nitrogen adsorption isotherms were performed at 77 K on a Micromeritics ASAP 2010 volumetric adsorption system. The BET surface area was deduced from the isotherm analysis in the relative pressure range 0.04 to 0.20.
39. ,Cullity, B. D.; Stock, S. R.Elements ofX-rayDiffraction; Prentice Hall: Englewood Cliffs, NJ, 2001; p 170.
40. Transmission electron microscopy was performed in a JEOL Mod. 2000 EX II microscope (200 kV).