Structural and Electrical Properties of the Perovskite Oxide Sr₂FeNbO₆

The mixed perovskite Sr 2 FeNbO 6 has been shown to have a tetragonal structure with space group I 4/ m (87), a = 5.6078(1) Å, c = 7.9658(1) Å, V = 250.51(1) Å 3 according to electron and X-ray diffraction. The material is redox stable and maintains its structure in a reducing atmosphere. After reducing in 5% H 2 at 900 °C for 6 h, Sr 2 FeNbO 6 still exhibits a tetragonal structure with space group I 4/ m (87), a = 5.6051(1) Å, c = 7.9644(1) Å, V = 250.22(1) Å 3, i.e., with a slightly higher degree of tetragonality. A lattice volume contraction of 0.12% was observed during the reduction, which may be attributed to the loss of lattice oxygen. TGA analysis indicates that Sr 2 FeNbO 6 starts to lose oxygen at 300 °C and the total weight loss is about 0.2 wt % from room temperature to 950 °C in 5% H 2 . The morphology of this material does not significantly change on reduction according to SEM observation. The conductivities of this material in air and 5% H 2 were 3.13 × 10 - 2 and 2.39 S/cm, respectively at 900 °C. The apparent conduction activation energy of Sr 2 FeNbO 6 in air is 0.74 ± 0.02 eV between 400 and 900 °C and in 5% H 2 is 0.28 ± 0.02 eV between 140 and 560 °C and 0.58 ± 0.02 eV between 560 and 900 °C, indicating it is a semiconductor in both atmospheres. The increase of dc conductivity of Sr 2 FeNbO 6 at low p (O 2 ) indicates n-type electronic conduction. The dc conductivity of Sr 2 FeNbO 6 at low p (O 2 ) exhibits a p (O 2 ) - 1/6 dependence that is interpreted by a simple defect chemistry model.