SHRINKAGE REDUCTION AND CRACK PREVENTION OF ALKALI-ACTIVATED PHOSPHOROUS SLAG CEMENT
Source abstract
Abstract
The effects of fly ash, calcium oxide and polypropylene fiber on the physical and mechanical properties, shrinkage and cracking behaviors of alkali-activated phosphorous slag cement (AA-PS-C) were studied. The results show that replacing 10 -15 % phosphorous slag by fly ash and adding calcium oxide as an expansive agent reduce the shrinkage of AA-PS-C. Fly ash will increase the flexural strength, although the compressive strength will be slightly decreased, while the calcium oxide expansive agent coated with aluminum stearate will slightly shorten the setting time and reduce the strength. Adding polypropylene fiber can greatly increase the crack-resistance of AA-PS-C. * Mass loss after being ignited at 950C for 20 min. * Prepared by adding 0.3 wt.% of polypropylene fiber (based on the sum of phosphorous slag and fly ash).
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Concrete and Cement Materials Research · Innovative concrete reinforcement materials · Concrete Properties and Behavior
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (9)
Show source-provided references
1. 10.1016/j.conbuildmat.2007.10.01110.1016/j.conbuildmat.2007.10.011 ↗
2. 10.1016/S0008-8846(97)00135-X10.1016/S0008-8846(97)00135-X ↗
3. 10.1016/j.cemconcomp.2004.09.02010.1016/j.cemconcomp.2004.09.020 ↗
4. 10.1016/j.cemconres.2008.11.01110.1016/j.cemconres.2008.11.011 ↗
5. 10.1016/j.cemconres.2006.11.02110.1016/j.cemconres.2006.11.021 ↗
6. 10.1016/j.cemconres.2004.06.03310.1016/j.cemconres.2004.06.033 ↗
7. 10.1016/S0008-8846(98)00236-110.1016/S0008-8846(98)00236-1 ↗
8. 10.1016/j.cemconres.2007.11.00210.1016/j.cemconres.2007.11.002 ↗
9. 10.14062/j.issn.0454-5648.2006.05.01910.14062/j.issn.0454-5648.2006.05.019 ↗