Effect of vibro-milling time and calcination condition on phase formation and particle size of nickel niobate nanopowders
Source abstract
Abstract
Abstract The effect of milling time on the phase formation and particle size of nickel niobate, NiNb 2 O 6 , powder synthesized by a solid-state reaction via a vibro-milling technique was investigated. Powder samples were characterized using DTA, XRD, SEM and laser diffraction techniques. It was found that the smallest particle size of 32 nm was achieved at 25 h of vibro-milling after which a higher degree of particle agglomeration was observed on continuation of milling to 35 h. In addition, by employing an appropriate choice of the milling time, a narrow particle size distribution curve was also observed.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Ferroelectric and Piezoelectric Materials · Microwave Dielectric Ceramics Synthesis · Electrical and Thermal Properties of Materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (12)
Show source-provided references
1. Low temperature synthesis of perovskite Pb(Ni1/3Nb2/3)O3 by hydrothermally-derived precursor10.1016/j.matlet.2004.12.021 ↗
2. Low-temperature properties of lead nickel-niobate ceramics10.1016/S0167-577X(01)00538-9 ↗
3. Phasic and microstructural developments of Pb(Ni1/3Nb2/3)O3 prepared by the columbite precursor process10.1016/0272-8842(95)00116-6 ↗
4. Effect of calcination conditions on phase formation and particle size of nickel niobate powders synthesized by solid-state reaction10.1016/j.matlet.2006.05.028 ↗
5. Effect of vibro-milling time on phase formation and particle size of lead titanate nanopowders10.1016/j.matlet.2005.11.043 ↗
6. Effect of calcination condition on phase formation and particle size of lead titanate powders synthesized by the solid-state reaction10.1016/j.matlet.2003.08.028 ↗
7. Klug · 1974
8. Phase and morphology evolution of corundum-type Ni4Nb2O9 powders synthesized by solid-state reaction10.1016/j.matlet.2006.09.056 ↗
9. Powder Diffraction File No. 76-2354. International Centre for Diffraction Data, Newtown Square, PA, 2000.
10. Phase and morphology evolution of magnesium niobate powders synthesized by solid-state reaction10.1016/j.matlet.2004.04.011 ↗
11. Effect of calcination conditions on phase formation and particle size of zinc niobate powders synthesized by solid-state reaction10.1016/j.matlet.2006.02.004 ↗
12. Effect of milling time on phase transition and grain growth during the annealing process of MA powders10.1016/j.msea.2004.12.015 ↗