Corrosion mechanisms of Al2O3/MgAl2O4 by V2O5, NiO, Fe2O3 and vanadium slag
Source abstract
Abstract
Abstract The effects of V2O5, NiO, Fe2O3 and vanadium slag on the corrosion of Al2O3 and MgAl2O4 have been investigated. The specimens of Al2O3 and MgAl2O4 with the respective oxides above mentioned were heated at 10 °C/min from room temperature up to three different temperatures: 1400, 1450 and 1500 °C. The corrosion mechanisms of each system were followed by XRD and SEM analyses. The results obtained showed that Al2O3 was less affected by the studied oxides than MgAl2O4. Alumina was only attacked by NiO forming NiAl2O4 spinel, while the MgAl2O4 spinel was attacked by V2O5 forming MgV2O6. It was also observed that Fe2O3 and Mg, Ni, V and Fe present in the vanadium slag diffused into Al2O3. On the other hand, the Fe2O3 and Ca, S, Si, Na, Mg, V and Fe diffused into the MgAl2O4 structure. Finally, the results obtained were compared with those predicted by the FactSage software.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Metallurgical Processes and Thermodynamics · Magnesium Oxide Properties and Applications · Advanced ceramic materials synthesis
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (17)
Show source-provided references
1. Refractory corrosion behavior under air–fuel and oxy–fuel environments
2. Corrosion resistance and microstructure of high-alumina refractories, based on the rotary slag test10.1111/j.1151-2916.1990.tb05159.x ↗
3. The microstructural features of an alumina–mullite–zirconia refractory material corroded by molten glass10.1016/S0272-8842(02)00137-2 ↗
4. Corrosion of high alumina and near stoichiometric spinels in iron-containing silicates slags10.1016/S0955-2219(02)00170-X ↗
5. Progress of petroleum coke combusting in circulating fluidized bed boilers—a review and future perspectives10.1016/j.resconrec.2006.03.012 ↗
6. Influence of blending methods on the co-gasification reactivity of petroleum coke and lignite10.1016/j.enconman.2010.11.009 ↗
7. Glass tank regenerators—modern refractory lining materials and attack from V2O5
8. Test of refractory materials for the condensation zone of regenerators10.4028/www.scientific.net/MSF.34-36.767 ↗
9. Sodium vanadate effect over refractory superstructures
10. Maun · J. Am. Ceram. Soc. · 1956 · 39 · 20710.1111/j.1151-2916.1956.tb15647.x ↗
11. Discontinuous dissolution of iron aluminate spinel in the Al2O3–Fe2O3 system10.1111/j.1151-2916.1995.tb08627.x ↗
12. Corrosion of spinel clinker by CaO–Al2O3–SiO2 ladle slag10.1016/S0955-2219(01)00509-X ↗
13. Design of NiO–MgO materials with different properties10.1039/B313500B ↗
14. FactSage™, Fact XML 5.2. CRCT and GTT-Technologies, Fact Sage Thermochemical Software and Database, Canada and Germany (2002).
15. Application of the FactSage to predict the ash melting behavior in reducing conditions10.1016/S1004-9541(07)60012-3 ↗
16. Muan · Am. J. Sci. · 1958 · 420
17. Valance reduction process from sol–gel V2O5 to VO2 thin films10.1016/S0169-4332(02)00180-0 ↗