Weakly agglomerated α-Al2O3 nanopowders prepared by a novel spray precipitation method
Source abstract
Abstract
Abstract In this paper, weakly agglomerated and well dispersed α-Al2O3 powders were synthesized by a novel spray precipitation method. It was demonstrated that the as-prepared powders exhibited better dispersity than powders from conventional precipitation due to the increased phase contact and reaction area during the precipitation process. The effects of different titration ways, calcination temperature and holding time on the morphology, phase composition and sintering behaviour of Al2O3 powders were systematically investigated. Weakly agglomerated and well crystallized α-Al2O3 powders were obtained when the as-prepared precursors were calcined at 1150 °C for 2 h in air. The average particle size of α-Al2O3 powders with higher sintering activity was approximately 68.6 nm, and the specific surface area was above 22.4 m2 g−1.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Advanced ceramic materials synthesis · Magnesium Oxide Properties and Applications · Microwave Dielectric Ceramics Synthesis
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (33)
Show source-provided references
1. Sintering of α-Al2O3 nanocrystalline ceramic from large α-Al2O3 polycrystalline nanoparticles10.1016/j.ceramint.2016.10.096 ↗
2. Cooperative luminescence from low temperature synthesized α-Al2O3: Yb3+ phosphor by using solution combustion10.1016/j.ceramint.2016.09.130 ↗
3. Effects of sintering aids on the transparency and conversion efficiency of Cr4+ Ions in Cr: YAG transparent ceramics10.1111/jace.13616 ↗
4. High dispersibility of α-Al2O3 powders from coprecipitation method by step-by-step horizontal ball-milling10.1007/s10854-017-7530-1 ↗
5. Effect of Er3+ concentration on the luminescence properties of Al2O3-ZrO2 powder10.1016/j.optmat.2016.11.020 ↗
6. Co-precipitated synthesis of Al2O3–ZrO2 composite ceramic nanopowders by precipitant and drying method regulation: a systematic study10.1016/j.ceramint.2014.08.098 ↗
7. Gas phase vibrational spectroscopy of the aluminum oxide anions (Al2O3)−
8. Investigation on the preparation and properties of monodispersed Al2O3 ZrO2 nanopowder via Co-precipitation method10.1016/j.jallcom.2016.03.265 ↗
9. Low temperature synthesis of nano alpha-alumina powder by two-step hydrolysis10.1016/j.materresbull.2015.08.021 ↗
10. Transformation kinetics of θ to α-phase of alumina powders prepared from different alumina salts by chemical processing10.1007/s10973-016-5410-1 ↗
11. Z. Li, K. Wu, J. Cao, et al., Controlled Synthesis of α-Al2O3 Via the Hydrothermal-Pyrolysis Method, 207 (1), 2017, p. 012004.10.1088/1757-899X/207/1/012004 ↗
12. Synthesis of yttria nano-powders by the precipitation method: the influence of ammonium hydrogen carbonate to metal ions molar ratio and ammonium sulfate addition10.1016/j.jallcom.2016.03.072 ↗
13. High sinterability nano-Y2O3 powders prepared via decomposition of hydroxyl-carbonate precursors for transparent ceramics10.1007/s10853-017-1071-0 ↗
14. The effect of novel synthetic methods and parameters control on morphology of nano-alumina particles10.1186/s11671-016-1472-z ↗
15. Heat transfer similarities between impinging jets and axial-flow impellers10.1134/S0040579516060130 ↗
16. Agitator dependent homogeneity enhancement of co-precipitation reaction for improving the dispersibility of precursors and Y2O3 powders10.1016/j.ceramint.2017.08.178 ↗
17. High optical quality Y2O3 transparent ceramics with fine grain size fabricated by low temperature air pre-sintering and post-HIP treatment10.1016/j.ceramint.2015.11.099 ↗
18. A novel spray co-precipitation method to prepare nanocrystalline Y2O3 powders for transparent ceramics
19. The effect of precipitant on co-precipitation synthesis of yttrium aluminum garnet powders10.1016/j.ceramint.2012.05.066 ↗
20. Mitigating the adverse effect of spray drying on the supersaturation generation capability of amorphous nanopharmaceutical powders10.1016/j.powtec.2015.02.059 ↗
21. Structural and phase transition of α-Al2O3 powders obtained by co-precipitation method10.1080/01411594.2015.1072628 ↗
22. The effect of precipitant on co-precipitation synthesis of yttrium aluminum garnet powders10.1016/j.ceramint.2012.05.066 ↗
23. A homogeneous co-precipitation method to synthesize highly sinterability YAG powders for transparent ceramics10.1016/j.ceramint.2014.10.076 ↗
24. Preparation of YAG nano-powders via an ultrasonic spray co-precipitation method10.1016/j.ceramint.2012.10.248 ↗
25. A new chemical route for the synthesis of nano-crystalline α-Al2O3 powder10.1016/S0955-2219(00)00322-8 ↗
26. Co-precipitation synthesis and spectroscopic studies of YAG and Yb:YAG nanopowder for opto-electronic applications
27. Fabrication of YAG transparent ceramics using carbonate precipitated yttria powder10.1016/j.jeurceramsoc.2015.02.014 ↗
28. Phase transition behavior of nanocrystalline Al2O3 powders10.4236/snl.2013.34012 ↗
29. Synthesis and characterization of mesoporous alumina with high specific area via coprecipitation method10.1016/j.vacuum.2016.08.005 ↗
30. A. Das, V. Sharma, Synthesis and Characterization of Eu3+ Doped α-Al2O3 Nanocrystalline Powder for Novel Application in Latent Fingerprint Development, 2016.10.5185/amlett.2016.6310 ↗
31. Preparation of YAG nanopowder by different routes and evaluation of their characteristics including transparency after sintering
32. Effects of drying method on preparation of nanometer α-Al2O310.1007/s11771-007-0065-5 ↗
33. Transparent Nd:YAG ceramics fabricated using nanosized γ-alumina and yttria powders10.1111/j.1551-2916.2008.02830.x ↗