Thermomechanical and thermophysical characteristics of alumina-carbon monolithic refractory containing surface-modified graphites in matrix
Source abstract
Abstract
Abstract The thermophysical and thermomechanical behavior of graphite-containing refractory castable matrix with 20.0 wt% of graphite had been compared with graphite-free high alumina based castable matrix analogous to it. The thermomechanical properties of similar type of castables with and without 5.0% of graphite had also been evaluated. Graphite was incorporated both as coated and as-received forms, the former having a thin sol-gel derived calcium aluminate coating on graphite flakes. The influence of thermal conductivity, thermal diffusivity and pore size distribution had been critically estimated. The changes in flexural strength, porosity and density of the matrices had also been determined to interpret the castable performance, namely refractoriness under load (RUL), spalling resistance and conventional physical properties. The role of coated graphite on improved densification and thermal tolerance of refractories was further explored by microstructure and phase evolution studies of all kinds of fired samples at 1500 °C. It was further supplemented with the scanning electron microscope (SEM) studies of surface-modified graphites at uncalcined and calcined condition.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Advanced ceramic materials synthesis · Aluminum Alloys Composites Properties · Recycling and utilization of industrial and municipal waste in materials production
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (52)
Show source-provided references
1. Carbon based refractories10.2109/jcersj.112.517 ↗
2. Microstructures and mechanical properties of Al2O3–C refractories with silicon additive using different carbon sources10.1016/j.msea.2010.12.066 ↗
3. The effect of additives on the properties and microstructures of Al2O3-C refractories10.1007/s10853-006-6770-x ↗
4. Young's modulus of elasticity of carbon-bonded alumina materials up to 1450 °C10.1111/jace.12526 ↗
5. Phase formation in Al2O3-C refractories with Al addition10.1016/j.jeurceramsoc.2016.11.027 ↗
6. Low-temperature preparation of titanium carbide coatings on graphite flakes from molten salts10.1111/j.1551-2916.2007.02184.x ↗
7. In-situ catalytic preparation and characterization of SiC nanofiber coated graphite flake with improved water-wettability10.1016/j.ceramint.2017.08.138 ↗
8. Synthesis and characterization of boehmitic alumina coated graphite by sol–gel method10.1016/j.ceramint.2008.11.006 ↗
9. Novel sol-gel process depositing α - Al2O3 for the improvement of graphite oxidation – resistance10.1016/S0040-6090(01)01259-7 ↗
10. Properties of Al2O3-C castable refractories with graphite powder coated with Al2O310.2109/jcersj.109.1267_270 ↗
11. Surface modification of graphite particles coated by atomic layer deposition and advances in ceramic composites10.1111/j.1744-7402.2012.02750.x ↗
12. Improvement of water/resin wettability of graphite using carbon black nano particles coating via ink media10.1016/j.jallcom.2009.04.019 ↗
13. Spinel-coated graphite for carbon containing refractory castables10.1111/j.1551-2916.2009.03133.x ↗
14. Improved sol-gel spinel (MgAl2O4) coatings on graphite for application in carbon containing high alumina castables10.1007/s10971-010-2275-9 ↗
15. Characteristics of refractory castables containing mullite and spinel coated graphites10.1080/10426914.2011.560501 ↗
16. Development of mullite and spinel coatings on graphite for improved water-wettability and oxidation resistance10.1016/j.ceramint.2010.03.035 ↗
17. Nanostructured cementitious sol gel coating on graphite for application in monolithic refractory composites10.1016/j.ceramint.2011.09.006 ↗
18. Comparison of solid state and sol-gel derived calcium aluminate coated graphite and characterization of prepared refractory composite10.1016/j.ceramint.2012.02.096 ↗
19. Significant improvement of refractoriness of Al2O3–C castables containing calcium aluminate nano-coatings on graphite10.1016/j.ceramint.2013.08.112 ↗
20. Nanoscale calcium aluminate coated graphite for improved performance of alumina based monolithic refractory composite10.1016/j.materresbull.2013.03.006 ↗
21. In depth studies on cementitious nanocoatings on graphite for its contribution in corrosion resistance of alumina based refractory composite10.1016/j.ceramint.2015.06.012 ↗
22. Thermal and thermomechanical characteristics of monolithic refractory composite matrix containing surface-modified graphite10.1016/j.ceramint.2015.12.155 ↗
23. Effect of surface-treated graphites on the properties of carbon containing monolithic refractory materials – a comprehensive comparison10.1111/ijac.12691 ↗
24. Thermomechanical characteristics of low carbon magnesia-based monolithic refractory containing nanostructured surface-modified graphites in matrix10.1080/0371750X.2017.1281765 ↗
25. Thermophysical properties of pressed and casted carbon-bonded alumina (Al2O3–C) up to 800 °C10.1002/adem.201300203 ↗
26. Thermomechanical behavior of high-alumina refractory castables with synthetic spinel additions10.1111/j.1151-2916.2000.tb01579.x ↗
27. Features and Future Development of the Carbon Containing Refractory, Key Engg. Mats. (Adv. Ceramics and composites)
28. Graphene oxide papers modified by divalent ions – enhancing mechanical properties via chemical crosslinking10.1021/nn700349a ↗
29. Calcium aluminate cements
30. Prediction of effective thermal conductivity of refractory materials at high temperatures based on synthetic geometry generation
31. Thermal expansion of Al2O3, BeO,MgO,B4C,SiC and TiC above 1000 °C10.1111/j.1151-2916.1959.tb12958.x ↗
32. Kingery · 1976 · 585
33. Thermal conductivity of packed beds of refractory particles: experimental results10.1111/j.1151-2916.1997.tb03094.x ↗
34. Expanded graphite as heat transfer matrix in metal hydride beds10.1016/S0360-3199(02)00057-5 ↗
35. Characterisation of powder beds by thermal conductivity: effect of gas pressure on the thermal resistance of particle contact points10.1002/ppsc.200400943 ↗
36. P. Das, S. Dutta, N. Das, S. Mukhopadhyay, Extended studies on surface-treated graphite vis-à-vis its application in high alumina refractory castable, Int. J. Appl. Ceram. Technol., 〈http://dx.doi.org/10.1111/ijac.12852〉, 2017.10.1111/ijac.12852 ↗
37. Improvement of thermal characteristics of refractory castable by addition of gel-route spinel nanoparticles10.1080/10426910601015998 ↗
38. Nano-bonded refractory castables10.1016/j.ceramint.2012.11.028 ↗
39. The heat conductivity of carbon-containing refractories10.1023/B:REFR.0000029623.05371.78 ↗
40. Oxidation mechanism of MgO–C in air at various temperatures10.1179/096797800680839 ↗
41. Improved thermal shock performance of Al2O3–C refractories due to nanoscaled additives10.1016/j.ceramint.2011.08.011 ↗
42. Low carbon carbon-bonded alumina refractories for functional components in steel technology
43. Strengthening mechanism of graphene oxide nanosheets for Al2O3–C refractories10.1016/j.ceramint.2013.05.117 ↗
44. Thermomechanical evaluation of self-flowing refractory castables with and without the addition of aluminate cement10.1016/j.ceramint.2011.12.062 ↗
45. Hot bending strength and creep behaviour at 1000–1400 °C of high alumina refractory castables with spinel, periclase and dolomite additions10.1016/j.jeurceramsoc.2008.05.044 ↗
46. Liquidus relations in the quaternary subsystem CaAl2O4–CaAl4O7–CaAl2SiO7–MgAl2O410.1111/j.1151-2916.1968.tb11828.x ↗
47. Effect of spinel content on hot strength of alumina-spinel castables in the temperature range 1000–1500 °C10.1016/S0955-2219(99)00042-4 ↗
48. Effect of preformed and in situ spinels on microstructure and properties of a low cement refractory castable10.1016/S0272-8842(03)00117-2 ↗
49. Toughening in graphene-ceramic composites10.1021/nn200319d ↗
50. Barsoum · 1997 · 505
51. Thermal resistance of grain boundaries in alumina ceramics and refractories10.1111/j.1151-2916.2003.tb03285.x ↗
52. Physical characteristics of alumina-carbon refractory castables containing calcium aluminate - coated graphites