Characterization of infrared transmittance in mixed transition metal oxides for solar cells application

Abstract The NiCo 2 O 4 spinel structure was successfully fabricated using wet chemical route followed by calcination at 300 °C. It was observed that the structure of NiCo 2 O 4 is highly dependent upon the temperature. At temperatures higher than 700 °C, NiCo 2 O 4 tends to release one oxygen and change from spinel to rock-salt structure. To obtain a thin film of nickel-cobalt oxides using RF-magnetron sputtering, a solid film was deposited on a glass substrate using the sintered oxide target with the same composition. Furthermore, the electrical conduction and crystallization of the sputtered oxide thin film was also affected by the annealing environment. After detailed characterization and understanding of the phase transformation, a nickel-cobalt oxide film with the lowest resistivity of 0.05 Ω cm and a high transmittance of 90% in the infrared range was finally obtained. In addition, NiCo 2 O 4 spinel thin films with high transmittance in infrared region were used for the front electrode of solar cells. As a result, the solar cells using IR-transparent NiCo 2 O 4 layer exhibit an improved quantum efficiency, which leads to a higher short circuit current density, J SC .