Thermal diffusivity of reaction-sintered AlON/Al2O3 particulate composites

Abstract The thermal diffusivity of particulate composites prepared by sintering compacts of Al 2 O 3 with additions of 1–25 mol% AlN under 1-atm nitrogen gas pressure at 1600–1800 °C has been measured over the range 25–1000 °C using the laser flash method. The diffusivity of reaction-sintered materials decreased on addition of AlN, mainly due to the formation of an AlON phase. This effect was less pronounced with increasing temperature and furthermore, it appeared to be related to the temperature-dependence of thermal resistance. The influence of crystalline phase, microstructure and physical property on the thermal diffusivity of AlON/Al 2 O 3 was characterized. The thermal conductivity of the sintered materials at room temperature behaved in a similar manner to the thermal diffusivity.