Bimodal grain structure effect on the static and dynamic mechanical properties of transparent polycrystalline magnesium aluminate (spinel)
Source abstract
Abstract
Abstract Transparent polycrystalline magnesium aluminate (spinel) with bimodal and unimodal grain structures were prepared. The influence of grain size distribution on static and dynamic mechanical properties were systematically investigated. The results showed that bimodal grain structure spinel has larger flexural strength (236.31 MPa) compared to unimodal grain structure spinel (221.38 MPa). Whereas, their values of hardness are very similar (15.1 vs 14.7 GPa) and fracture toughness remains unchanged (1.1 MPa∙m1/2 for both spinel). Although static compression strength of bimodal grain structure spinel (1236 MPa) is higher than that of unimodal one (1078 MPa) due to a smaller average grain size in the former, the negative effect of bimodal grain structure reduced the spinel strength compared to theoretically predicted value. Bimodal grain structure spinel shows slightly lower increment (49%) in compression strength from static to dynamic loading compared to that of unimodal one (57%) due to a decreased strain-rate sensitivity ascribed to bimodal grain structure. A brittle mode in inelastic deformation at Hugoniot elastic limit was demonstrated in both bimodal and unimodal grain structures. Bimodal grain structure has an influence on the Hall-Petch-like relation of yield strength under planar impact loading.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Advanced ceramic materials synthesis · High-Velocity Impact and Material Behavior · Aluminum Alloys Composites Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (35)
Show source-provided references
1. Effect of grain size on brittle and semibrittle strength: implications for micromechanical modelling of failure in compression10.1029/JB095iB07p10907 ↗
2. Effect of grain morphology and grain size on the mechanical properties of Al2O3 ceramics10.1007/BF00355953 ↗
3. Effect of grain size on the static and dynamic mechanical properties of magnesium aluminate spinel (MgAl2O4)10.1016/j.jeurceramsoc.2017.04.025 ↗
4. Ceramic tensile strength-grain size relations: grain sizes, slopes, and branch intersections10.1023/A:1018511613779 ↗
5. The effect of grain size on the mechanical and optical properties of spark plasma sintering-processed magnesium aluminate spinel MgAl2O410.1111/j.1744-7402.2012.02849.x ↗
6. Surface-finish effects on strength-vs-grain-size relations in polycrystalline Al2O310.1111/j.1151-2916.1974.tb10866.x ↗
7. Evaluation of hot pressing and hot isostastic pressing parameters on the optical properties of spinel10.1111/j.1551-2916.2005.00527.x ↗
8. Recent advances in spinel optical ceramic
9. High-strength transparent spinel with fine, unimodal grain size
10. Densification and microstructure evolution of reactively sintered transparent spinel ceramics
11. Fine-grained transparent spinel windows by the processing of different nanopowders10.1111/j.1551-2916.2010.03814.x ↗
12. Mechanical properties of magnesia-spinel composites10.1016/S0955-2219(01)00373-9 ↗
13. Microstructural and mechanical properties of nanocrystalline spinel and related composites10.1016/S0272-8842(01)00071-2 ↗
14. Transmission physics and consequences for materials selection, manufacturing, and applications10.1016/j.jeurceramsoc.2008.03.025 ↗
15. Grain size effect on the mechanical properties of transparent spinel ceramics10.1016/j.jeurceramsoc.2012.09.024 ↗
16. ASTM C-1327-15 · 2015
17. ASTM C-1161-13 · 2013
18. ASTM C 1421-10 · 1999
19. Pulse shaping techniques for testing brittle materials with a split hopkinson pressure bar10.1007/BF02411056 ↗
20. Hopkinson techniques for dynamic recovery experiments
21. Compression-induced microcrack growth in brittle solids: axial splitting and shear failure10.1029/JB090iB04p03105 ↗
22. The failure of brittle solids containing small cracks under compressive stress states10.1016/0001-6160(86)90086-6 ↗
23. Comparison of calculated and observed crack densities and seismic velocities in westerly granite10.1029/JB081i020p03484 ↗
24. Direct observation of the dynamic compressive failure of a transparent polycrystalline ceramic (AlON)10.1111/j.1551-2916.2006.00965.x ↗
25. Dynamic response of transparent ceramic MgAl2O4 spinel10.1016/j.scriptamat.2011.07.044 ↗
26. Rate effects on the mechanical response of magnesium aluminate spinel10.1016/j.msea.2011.03.027 ↗
27. An interacting micro-crack damage model for failure of brittle materials under compression10.1016/j.jmps.2007.06.012 ↗
28. Grady · 1993
29. On the shear strength of shock loaded brittle solids10.1063/1.357731 ↗
30. Relationship between impact yield stress and indentation hardness10.1063/1.321790 ↗
31. Shock deformation of coarse grain alumina above hugoniot elastic limit10.1007/s10853-010-4409-4 ↗
32. Electron microscopy of shock deformation in alumina10.1016/j.ceramint.2011.03.034 ↗
33. The onset of twinning in metals: a constitutive description10.1016/S1359-6454(01)00300-7 ↗
34. High strain-rate response of commercially pure vanadium10.1016/S0167-6636(99)00056-3 ↗
35. Tantalum and vanadium response to shock-wave loading at normal and elevated temperatures. Non-monotonous decay of the elastic wave in vanadium10.1063/1.4885047 ↗