Ablation mechanism of WC-SiC double layer coating under oxyacetylene torch test

Abstract A WC-SiC double-layer coating was prepared on C/C composites to improve their anti-ablation property. The WC outer layer was designed to withstand high heat flux by its high mechanical strength, the SiC inner layer could transform into SiO 2 to block oxygen by its good anti-oxygen permeability. During ablation process, amounts of SiO 2 filled into the pores and cracks of WC outer layer, forming a steadily self-filling and cooling structure. As a result, the mass and linear ablation rates of WC-SiC coated C/C composites were 0.013 mg s −1 cm 2 and −1.61 µm/s, respectively. Compared with single SiC coated and single WC coated C/C composites, the linear ablation rates decreased by 46.3% and 27.3%, respectively, indicating that WC-SiC coating has a remarkable effect to resist chemical and mechanical ablation.