Degradation mechanisms of alumina–silica runner refractories by carbon steel during ingot casting process

Liugang Chen, Annelies Malfliet, Peter Tom Jones, Bart Blanpain, Muxing Guo

Ceramics International· Volume 42· Issue 8
Publisher page

Abstract

Abstract The corrosion behavior of alumina-silica (Al 2 O 3 –SiO 2 ) refractories by liquid carbon steel was studied. This was performed by a refractory crucible test in a vacuum induction furnace at 1520–1545 °C under reducing atmosphere. The results indicate that Mn, Si and a minor amount of Fe in the steel were oxidized at steel/refractory interface, combing with refractory components to form a MnO–SiO 2 –Al 2 O 3 –based slag. This slag was liquid at the testing temperature, and infiltrated along the open-pore network and the grain boundaries into the Al 2 O 3 –SiO 2 refractories. Both Al 2 O 3 –rich and Al 2 O 3 –SiO 2 aggregates in the refractories dissolved into the infiltrating slag. As a result, the refractories were structurally weakened and residual Al 2 O 3 –rich and Al 2 O 3 –SiO 2 aggregates in the hot face of the refractories were washed away into the liquid steel, affecting steel quality.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Metallurgical Processes and Thermodynamics · Microstructure and Mechanical Properties of Steels · Metal Alloys Wear and Properties

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (18)

Show source-provided references
1. The role of mullite-based refractory chemical interactions on the formation of exogenous non-metallic inclusions in vacuum treated 0.3% C steel10.2355/isijinternational.47.392 ↗
2. Studies of the wetting characteristics of liquid iron on dense alumina by the X-ray sessile drop technique10.1007/s11663-003-0006-0 ↗
3. Interfacial phenomena in some slag-metal reactions10.1007/s11663-000-0073-4 ↗
4. Inclusion characteristics of bearing steel in a runner after ingot casting10.1002/srin.200900106 ↗
5. Large inclusions in plain-carbon steel ingots cast by bottom teeming10.2355/isijinternational.46.670 ↗
6. Effect of processing parameters on the origin of nonmetallic inclusions
7. Effect of different casting parameters on the cleanliness of high manganese steel ingots compared to high carbon steel10.1007/s11661-013-1949-7 ↗
8. Comparison of the chemical corrosion resistance of magnesia-based refractories by stainless steelmaking slags under vacuum conditions10.1016/j.ceramint.2015.08.175 ↗
9. Degradation mechanisms of magnesia-chromite refractories by high-alumina stainless steel slags under vacuum conditions10.1016/j.jeurceramsoc.2005.12.025 ↗
10. Laboratory induction furnace to study refractory materials degradation in a controlled atmosphere at high temperature
11. FactSage thermochemical software anddatabases10.1016/S0364-5916(02)00035-4 ↗
12. Surface tension of liquid iron and iron-oxygen alloys10.1179/cmq.1983.22.1.9 ↗
13. Interaction between steel and distinct gunning materials in the tundish10.2355/isijinternational.54.2551 ↗
14. The influence of ZnO in fayalite slag on the degradation of magnesia-chromite refractories during secondary Cu smelting10.1016/j.jeurceramsoc.2015.03.013 ↗
15. Verein Deutscher Eisenhüttenleute (VDEh), Slag Atlas, Verlag Stahleisen GmbH, Düsseldorf, 1995, pp. 116.
16. Osborn · 1960
17. Equilibrium relationships on the liquids surface in part of the MnO–Al2O3–SiO2 system10.1111/j.1151-2916.1943.tb15177.x ↗
18. Al2O3 region of ternary aluminosilicate systems I: the FeO–Al2O3–SiO2 and MnO-–Al2O3–SiO2 systems