Aqueous processing of Ce0.8Sm0.2O1.9 green tapes
Source abstract
Abstract
Abstract An aqueous tape casting of Ce 0.8 Sm 0.2 O 1.9 (SDC) ceramics was developed using poly(acrylic acid) (PAA) as dispersant, poly(vinyl alcohol) (PVA) as binder, poly(ethylene glycol) (PEG) as plasticizer, and deionized water as solvent. Surface properties of SDC powder with and without PAA dispersant were characterized by electrokinetic measurements. The rheology of the SDC slurries was evaluated with a rotary viscometer. The zeta potential measurement showed that the isoelectric point (IEP) for SDC powders in the absence of dispersant corresponds to a pH value of 3.66. The experimental results showed that the pH value greatly affects the rheology of the slurry. The optimum content to get a stable dispersed slurry is 2 wt% PAA in pH value range of 9–10. In presence of 2 wt% PAA dispersant, 55 wt% SDC powders exhibited shear thinning behavior, indicating that SDC slurry was homogenous and well stabilized. Homogeneous, smooth, and defect-free green tapes were successfully obtained by an appropriate slurry formula.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Advancements in Solid Oxide Fuel Cells · Electronic and Structural Properties of Oxides · Nuclear materials and radiation effects
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (20)
Show source-provided references
1. Oxygen transport and exchange in oxide ceramics10.1016/0378-7753(93)01789-K ↗
2. Ceramic fuel cells10.1111/j.1151-2916.1993.tb03645.x ↗
3. High-temperature fuel cell with ceria–yttria solid electrolyte10.1149/1.2096212 ↗
4. Study of a solid-oxide fuel cell with a ceria-based solid electrolyte10.1016/0167-2738(89)90310-X ↗
5. Synthesis and characterization of (CeO2)0.8(SmO1.5)0.2 thin films for polymeric precursors10.1149/1.2221125 ↗
6. Electrical properties and reproducibilities of ceria–rare-earth oxide systems and their application to solid oxide fuel cell10.1016/0167-2738(89)90061-1 ↗
7. Enhanced ceria: a low temperature SOFC electrolyte10.1016/0167-2738(92)90103-V ↗
8. The electrical conductivity of CaO-doped nonstoichiometric cerium dioxide from 700 to 1500°C10.1149/1.2403668 ↗
9. On the green density, sintering behavior and electrical property of tape cast Ce0.9Gd0.1O1.95 electrolyte film10.1016/S0025-5408(02)00931-5 ↗
10. Aqueous colloidal processing and green sheet properties of lead zirconate titanate (PZT) ceramics made by tape casting10.1016/S0955-2219(03)00460-6 ↗
11. Aqueous tape casting of 10 mol%-Gd2O3-doped CeO2 nano-particles10.1016/j.msea.2006.05.073 ↗
12. Aqueous tape casting of alumina substrates10.1016/0955-2219(93)90098-C ↗
13. Aqueous processing of titanium carbide green sheets10.1111/j.1151-2916.2001.tb01049.x ↗
14. Effect of 2-phosphonobutane-1,2,4-tricarboxylic acid adsorption on the stability and rheological properties of aqueous nanosized 3-mol%-yttria-stabilized tetragonal-zirconia polycrystal suspensions10.1111/j.1151-2916.2003.tb03432.x ↗
15. Colloidal processing of ceramics10.1111/j.1151-2916.2000.tb01560.x ↗
16. Schindler · 1981
17. Rahaman · 1995
18. Preparation of aluminum nitride green sheet by aqueous tape casting10.1016/j.ceramint.2003.11.014 ↗
19. Reed · 1995
20. Aqueous processing and mechanical properties of PLZT green tapes10.1016/S0921-5093(00)00701-2 ↗