Luminescence properties of Ce3+-doped and Ce3+–Tb3+ co-doped Na0.34Ca0.66Al1.66Si2.34O8 phosphor for UV-LED

Abstract Ce 3+ -doped and Ce 3+ –Tb 3+ co-doped Na 0.34 Ca 0.66 Al 1.66 Si 2.34 O 8 (NCASO) phosphors have been synthesized via a high temperature solid-state reaction method. The samples were measured by using X-ray diffraction (XRD), photoluminescence (PL) and photoluminescence excitation (PLE) spectra. The results of XRD indicated that the as-prepared samples were pure NCASO phosphors. The Ce 3+ -doped NCASO phosphor exhibited an intense blue emission centered at 414 nm under 335 nm excitation. The optimal doping concentration of Ce 3+ in NCASO was confirmed 0.75 mol%. The concentration quenching occurs beyond 0.75 mol% of Ce 3+ because of electric quadrupole–quadrupole interaction between Ce 3+ ions. To tune the luminescent color of NCASO:Ce 3+ phosphor, Tb 3+ ions were introduced into the lattice of NCASO:Ce 3+ phosphor. It was found the emission intensity of Ce 3+ ions decreases gradually with the increase of Tb 3+ ions concentration owing to energy transfer from Ce 3+ to Tb 3+ . Moreover, the emitting colors can be adjusting from blue to green. The electric dipole–dipole interaction was induced to be responsible for energy transfer between Ce 3+ to Tb 3+ . These results show that NCASO:Ce 3+ , Tb 3+ phosphors can be used as a potential single-phased white-emitting candidate for UV WLEDs.