Paper-derived hydroxyapatite
Source abstract
Abstract
Abstract Porous hydroxyapatite structures were manufactured via a novel preceramic paper process. Preceramic paper sheets were produced from aqueous suspensions loaded with different contents of pulp fiber and HA filler. Pressure loading was applied in order to increase the packing density in the paper sheets. The paper sheets were sintered at 1250 °C for 1 h. The porous ceramic specimens were characterized for density, porosity, microstructure and mechanical properties. A pronounced volumetric shrinkage was observed, but no surface flaws or inhomogeneous areas were detected. The mechanical strength using the ball on three balls test (B3B test) and elastic modulus of sintered specimens vary between 18 and 28 MPa and 0.65–1.53 GPa, respectively.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Bone Tissue Engineering Materials · Additive Manufacturing and 3D Printing Technologies · Dental materials and restorations
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (19)
Show source-provided references
1. Preceramic paper-derived ceramics10.1111/j.1551-2916.2008.02752.x ↗
2. Laminated object manufacturing (LOM) of Si–SiC composite10.1002/adem.200400112 ↗
3. Laminated object manufacturing of preceramic-paper-derived Si–SiC composites10.1002/adma.200700789 ↗
4. LZSA glass–ceramic laminates: fabrication and mechanical properties10.1016/j.jmatprotec.2007.12.011 ↗
5. Preceramic paper derived alumina/zirconia ceramics10.1002/adem.201100017 ↗
6. Paper-derived bioactive glass tape
7. Heat-resistant insulating papers based on inorganic fibers
8. Paper pulp waste—a new source of raw material for the synthesis of a porous ceramic composite10.1007/BF02708014 ↗
9. Biaxial tensile strength test for brittle rectangular plates10.2109/jcersj.114.1054 ↗
10. Paper physics
11. The effect of particle size and shape of paper fillers on paper properties
12. The paper surface in relation to the network
13. Anisotropic shrinkage of cordierite-type glass powder cilindrical compacts10.1557/JMR.1988.0122 ↗
14. Anisotropic shrinkage in tape-cast alumina: role of processing parameters and particle shape10.1111/j.1151-2916.1999.tb02132.x ↗
15. Constrained densification kinetics of alumina/borosilicate glass plus alumina/alumina sandwich structure10.1111/j.1151-2916.2002.tb00057.x ↗
16. Biodegradable and bioactive porous polymer/inorganic composite scaffolds for bone tissue engineering10.1016/j.biomaterials.2006.01.039 ↗
17. Fabrication of 13-93 bioactive glass scaffolds for bone tissue engineering using indirect selective laser sintering10.1088/1758-5082/3/2/025004 ↗
18. Tensile strength of bovine trabecular bone10.1016/0021-9290(85)90027-2 ↗
19. Multiaxial strength characteristics of trabecular bone10.1016/0021-9290(83)90083-0 ↗