Fabrication of a SiC/Si/MoSi2 multi-coating on graphite materials by a two-step technique

Abstract A SiC/Si/MoSi 2 multi-coating for graphite materials was prepared by a two-step technique. SiC whisker reinforcement coating was produced by pyrolysis of hydrogen silicone oil (H-PSO) at 1600 °C, and then the dense coating was formed by embedding with the powder mixture of Si, graphite and MoSi 2 at 1600 °C in argon atmosphere. The microstructure, thickness, phase and oxidation resistance of the coating were investigated. Research results showed that, the phase of multi-coating was composed of SiC, Si and MoSi 2 . The thickness of the coating was about 300 μm. In addition, the coating combined with matrix well, and surface was continuous and dense. The oxidation pretreatment experiment was carried out in the static air at 1400 °C for 4 h before thermal failure tests and the specimens had 0.045% weight gain. Subsequent thermal failure tests showed that, the SiC/Si/MoSi 2 multi-coating had excellent anti-oxidation property, which could protect graphite materials from oxidation at 1000 °C in air for 12 h and the corresponding weight loss was below 1 wt%. Based on the surface morphology changes, oxidation pretreatment experiment and thermal failure tests enhanced densification of multi-coating and the coating had a certain self-healing ability.