Crack tolerant silicon carbide ceramics prepared by liquid-phase assisted oscillatory pressure sintering

Abstract Silicon carbide ceramics were prepared by liquid-phase assisted oscillatory pressure sintering (OPS) with graphene and in-situ synthesized SiC whisker as the reinforcements. The effects of sintering temperature on the densification, morphology and mechanical performances of the SiCp-SiCw-graphene ceramics were investigated. In the temperature range from 1700 to 1800 °C, the densification rate of SiCp-SiCw-graphene ceramics was accelerated, ascribing to the reduction in viscosity of the glassy phase. At 1800 °C, the flexural strength and fracture toughness of the OPS ceramics corresponded to 697 MPa and 5.8 MPa m1/2, respectively, which were higher than that of the hot-pressed ceramics under the same temperature conditions. Multiphase toughening mechanisms, such as whisker bridging and pullout, graphene bridging and delamination, were considered as the primary mechanisms. This work demonstrates an effective strategy to prepare silicon carbide ceramics at low sintering temperature.