Combustion synthesis of high porosity SiC foam with nanosized grains

Abstract High porosity silicon carbide (SiC) foam with nanosized grains was synthesized by a newly developed process involving two steps: (i) preparation of Si/C foam by gel-casting technique and (ii) fabrication of SiC foam by combustion Si/C foam in nitrogen atmosphere. The as-synthesized SiC foam with a high porosity in the range 70–90% exhibited an attractive strength up to 1.6 MPa. SEM analysis showed that the foam struts consisted of tightly bonded SiC particles with a grain size of 80–300 nm.