In situ preparation of SiC/Si3N4-NW composite powders by combustion synthesis

Abstract Large-scale composite powders containing silicon carbide (SiC) particles and silicon nitride nanowires (Si 3 N 4 -NWs) were synthesized in situ by combustion synthesis (CS). In this process, a mixture of silicon, carbon black, polytetrafluoroethylene (PTFE) and a small amount of iron powders was used as the precursor. The products were characterized by XRD, SEM, EDS and TEM. The particles are equiaxed with diameters in the micron range, and the in situ formed nanowires are straight with uniform diameters of 20–350 nm and lengths of tens of microns. The Si 3 N 4 -NWs are characterized to be α-phase single crystals grown along the [1 0 1] or [1 0 0] direction. VLS and SLGS processes are proposed as the growth mechanisms of the nanowires. The as-synthesized powders have great potential for use in the preparation of high-performance SiC/Si 3 N 4 -NW composites.