Centrifugal casting of Al2O3–15 wt.%ZrO2 ceramic composites

Abstract Aqueous ceramic slurries with different solid contents (60, 70 and 78 wt.%) were prepared by mixing 85 wt.% low-temperature-sinterable high purity α-alumina and 15 wt.% ZrO 2 (3 mol% Y 2 O 3 ) in distilled water and a small amount of poly-carboxylic ammonium as the dispersion agent. Consolidation was performed by using a high-speed centrifugal casting process at 4000 rpm for 1 h. The result showed that the dispersion agent had a great influence on the viscosities of the slurries. It was also observed that the green and sintered densities of the Al 2 O 3 –15 wt.%ZrO 2 composites increased with the solid contents. Phase segregation could be effectively eliminated when the solid content of the slurry was 78 wt.%.