Preparation of alumina by aqueous gelcasting

Abstract The alumina ceramic was prepared by aqueous gelcasting. The effects of zeta potentials, solid loading, dispersant content and milling time on the alumina suspension were studied systematically. The dispersant content has remarkable effects on the viscosity of the suspension. The appropriate dispersant concentration for alumina aqueous slurry with the solid loading of 55 vol.% is 0.6 wt.%. It can be seen that all suspensions (50–56 vol.% solid loading) exhibited a shear-thinning behavior and relatively low viscosity, which was suitable for casting. The degree of shear thinning and the viscosity at high shear rates increased with increasing volume fraction of solid. As the milling time prolongs, viscosity of the suspension decreases first, then the plateau appears and the average diameter keeps changeless. When the milling time was shorter than 20 h, the viscosity of slurries decreased gradually as the time of milling increased. After 20 h milling, the viscosity of the slurry tended to be consistent. Therefore, the ball milling time should be equal to or more than 20 h to obtain a stable suspension at equilibrium. The time available for casting the slurry (idle time) can be controlled by the amounts of initiator and catalyst added to the slurry as well as by the processing temperature. Micrograph of the gelcast green body was homogeneous.