High performance electrochemical H2O2 sensor based on MWCNT thin films fabricated by novel electron beam evaporation

Abstract High quality multi-walled carbon nanotubes (MWCNT) were grown by electron beam evaporation (EBE) under a high vacuum of 10 −6 mtorr. The influence of deposition thickness on the orientation, morphology and vibrational bands of MWCNT films fabricated on tantalum (Ta) substrate was discussed. XRD patterns of the film revealed the presence of (002) preferential plane of carbon. Raman spectral analysis show the G-band Raman feature corresponding to high frequency E 2 g of first order mode, suggesting that CNTs were composed of crystalline carbon. SEM image of 200 nm thick MWCNT film shows well shaped homogenous fine nanotubes of length ~300 nm and diameter ~70 nm with high purity. The electrochemical performance of the MWCNTs/Ta electrodes was studied by cyclic voltammetry. The sensor prepared with optimum thickness can detect H 2 O 2 in the wide range covering 5 µM to 0.025 mM, with the detection limit as low as 0.09 µM. The results demonstrate that the fabrication of MWCNTs/Ta electrode by EBE is a very interesting and useful approach, likely to be a focus of upcoming research efforts in electrochemical sensing.