Osteoblast behaviour on zirconia fabricated by additive and subtractive technology
Source abstract
Abstract
Zirconia is an attractive material for the manufacturing of oral implants and patient-individual barriers for guided bone regeneration. This study compared osteoblast behaviour on additive manufactured and milled 3-mol% yttria-stabilized tetragonal polycrystal zirconia (ZrO2). Two groups of samples (Ø5 × 2 mm) were manufactured by stereolithography (LithaCon 230, Lithoz, Vienna, Austria) and subsequently heat-treated and sintered. One group remained superficially unmodified (AM-ZrO2-unmod.), while the other was polished according to DIN EN ISO 6872 standard using automated grinding (AM-ZrO2-pol.). For comparison, milled samples (e.max ZirCAD LT, Ivoclar Vivadent, Schaan, Liechtenstein) were sintered and polished similarly (Mil-ZrO2-pol.). Surface roughness was characterized using tactile profilometry. Adhesion, proliferation and coverage of human fetal osteoblasts (hFOB 1.19) as well as expression of osteogenic marker genes ALPL and RUNX2 were determined (and statistically compared using Kruskal-Wallis-analyses and Dunn's Post-hoc-tests). The surface roughness of AM-ZrO2-unmod. Was 45 times higher than that of the polished groups. No significant differences were detected between the three groups regarding cell adhesion and proliferation. With regard to cell coverage, AM-ZrO2-pol. Significantly outperformed the two other groups (p < 0.05). ALPL- and RUNX2-mRNA expression was insignificantly superior for AM-ZrO2-unmod. Compared to the two other groups. Therefor no detrimental effect on osteoblast behaviour caused by the investigated, acrylic binder-based 3D printing workflow was observed.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Bone Tissue Engineering Materials · Dental materials and restorations · Additive Manufacturing and 3D Printing Technologies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (56)
Show source-provided references
1. On the behaviour of zirconia-based dental materials: a review10.1016/j.jmbbm.2021.104861 ↗
2. In vitro biofilm formation on titanium and zirconia implant surfaces10.1902/jop.2016.160245 ↗
3. Titanium and zirconium release from titanium- and zirconia implants in mini pig maxillae and their toxicity in vitro10.1016/j.dental.2020.01.013 ↗
4. Ligature-induced peri-implant bone loss around loaded zirconia and titanium implants10.11607/jomi.7015 ↗
5. Slip-cast zirconia dental roots with tunnels drilled by laser process10.1016/0022-3913(90)90326-8 ↗
6. Biomechanical studies on newly tailored artificial dental root
7. Three-dimensional computerized stress analysis of commercially pure titanium and yttrium-partially stabilized zirconia implants
8. Performance and outcome of zirconia dental implants in clinical studies: a meta-analysis10.1111/clr.13352 ↗
9. Clinical outcomes of zirconia dental implants: a systematic review10.1177/0022034516664043 ↗
10. A prospective clinical cohort investigation on zirconia implants: 5-year results10.3390/jcm9082585 ↗
11. The injection moulding of fine and ultra-fine zirconia powders10.1016/0272-8842(95)96204-3 ↗
12. Influence of debinding rate, solid loading and binder formulation on the green microstructure and sintering behaviour of ceramic injection mouldings10.1016/S0272-8842(97)00039-4 ↗
13. Additive technology: update on current materials and applications in dentistry10.1111/jopr.12510 ↗
14. 2017
15. 3D-printing zirconia implants; a dream or a reality? An in-vitro study evaluating the dimensional accuracy, surface topography and mechanical properties of printed zirconia implant and discs10.1016/j.jmbbm.2017.08.018 ↗
16. Bone response to conventional titanium implants and new zirconia implants produced by additive manufacturing
17. Ceramic printing - comparative study of the flexural strength of 3D printed and milled zirconia Int J Prosthodont
18. The flexural strength and flexural modulus of stereolithography additively manufactured zirconia with different porosities10.1111/jopr.13430 ↗
19. Additive manufacturing of zirconia ceramics: a state-of-the-art review10.1016/j.jmrt.2020.05.131 ↗
20. Human gingival fibroblast and osteoblast behavior on groove-milled zirconia implant surfaces10.3390/ma15072481 ↗
21. Clinical outcomes of root-analogue implants restored with single crowns or fixed dental prostheses: a retrospective case series10.3390/jcm9082346 ↗
22. In silico evaluation of the stress fields on the cortical bone surrounding dental implants: comparing root-analogue and screwed implants10.1016/j.jmbbm.2020.103667 ↗
23. A zirconia implant-crown system: a case report
24. Loaded custom-made zirconia and titanium implants show similar osseointegration: an animal experiment10.1902/jop.2004.75.9.1262 ↗
25. Immediate, non-submerged, root-analogue zirconia implant in single tooth replacement10.1016/j.ijom.2007.11.008 ↗
26. Immediate, non-submerged, root-analogue zirconia implants placed into single-rooted extraction sockets: 2-year follow-up of a clinical study10.1016/j.ijom.2009.07.008 ↗
27. Root analog zirconia implants: true anatomical design for molar replacement--a case report
28. Immediate, single stage, truly anatomic zirconia implant in lower molar replacement: a case report with 2.5 years follow-up10.1016/j.ijom.2010.08.003 ↗
29. Innovative single-tooth replacement with an individual root-analog hybrid implant in the esthetic zone: case report10.11607/jomi.5562 ↗
30. Designing a novel dental root analogue implant using cone beam computed tomography and CAD/CAM technology10.1111/j.1600-0501.2011.02359.x ↗
31. A novel root analogue dental implant using CT scan and CAD/CAM: selective laser melting technology10.1016/j.ijom.2012.01.014 ↗
32. Immediate, non-submerged, root-analogue direct laser metal sintering (DLMS) implants: a 1-year prospective study on 15 patients
33. Custom-made root-analogue zirconia implants: a scoping review on mechanical and biological benefits10.1002/jbm.b.34147 ↗
34. Customized-3D zirconia barriers for guided bone regeneration (GBR): clinical and histological findings from a proof-of-concept case series10.1016/j.jdent.2021.103780 ↗
35. Effect of milled and lithography-based additively manufactured zirconia (3Y-TZP) on the biological properties of human osteoblasts
36. Behavior of SaOS-2 cells cultured on different titanium surfaces10.1177/154405910308200907 ↗
37. Response of human bone marrow stromal cells, MG-63, and SaOS-2 to titanium-based dental implant surfaces with different topography and surface energy10.1111/j.1600-0501.2011.02328.x ↗
38. Requirement for both micron- and submicron scale structure for synergistic responses of osteoblasts to substrate surface energy and topography10.1016/j.biomaterials.2007.02.024 ↗
39. Crystal structure of zirconia affects osteoblast behavior10.1016/j.dental.2020.04.017 ↗
40. Strength and reliability of zirconia fabricated by additive manufacturing technology10.1016/j.dental.2022.07.004 ↗
41. NIH Image to ImageJ: 25 years of image analysis10.1038/nmeth.2089 ↗
42. Analysis of relative gene expression data using real-time quantitative PCR and the 2(-Delta Delta C(T)) Method10.1006/meth.2001.1262 ↗
43. In vitro surface characteristics and impurity analysis of five different commercially available dental zirconia implants10.1186/s40729-018-0124-8 ↗
44. Effect of various polishing burs on surface roughness and bacterial adhesion in pediatric zirconia crowns10.4012/dmj.2018-106 ↗
45. Effect of clinically relevant CAD/CAM zirconia polishing on gingival fibroblast proliferation and focal adhesions
46. Comparison of peri-implant bone formation around injection-molded and machined surface zirconia implants in rabbit tibiae10.4012/dmj.2015-024 ↗
47. 3D printed zirconia dental implants with integrated directional surface pores combine mechanical strength with favorable osteoblast response10.1016/j.actbio.2022.07.030 ↗
48. Additively manufactured zirconia for dental applications10.3390/ma14133694 ↗
49. Effects of titanium surface topography on bone integration: a systematic review10.1111/j.1600-0501.2009.01775.x ↗
50. Surface structure of zirconia implants: an integrative review comparing clinical results with preclinical and in vitro data10.3390/ma15103664 ↗
51. The influence of surface roughness of titanium on beta1- and beta3-integrin adhesion and the organization of fibronectin in human osteoblastic cells10.1016/j.biomaterials.2004.07.054 ↗
52. Attempted caveolae-mediated phagocytosis of surface-fixed micro-pillars by human osteoblasts10.1016/j.biomaterials.2015.10.030 ↗
53. 3D printing of ceramics: a review10.1016/j.jeurceramsoc.2018.11.013 ↗
54. Understanding dental CAD/CAM for restorations--dental milling machines from a mechanical engineering viewpoint. Part B: labside milling machines
55. A critical review of dental implant materials with an emphasis on titanium versus zirconia10.3390/ma8030932 ↗
56. Digital dentistry: an overview of recent developments for CAD/CAM generated restorations10.1038/sj.bdj.2008.350 ↗