High strength silica-based ceramics material for investment casting applications: Effects of adding nanosized alumina coatings

Abstract A nanosized alumina coating was synthesized on the surface of fused silica particles by electrostatic attraction. The effects of the coated fused silica particles on the cristobalite crystallization behavior, microstructure evolution, and flexural strength of silica-based ceramic cores were investigated. X-ray diffraction (XRD) was used to characterize phase transformations in the specimens, and the results indicated that the formed nanosized alumina coatings could retard cristobalite formation by inducing compressive stress on the fused silica particle surface. A mullite phase was also found due to the reaction of the nanosized alumina coating and the surface of the fused silica when the sintering temperature was increased to 1300 °C. Analysis using scanning electron microscopy equipped with energy dispersive spectrometry (SEM/EDS) suggested that alumina nanoparticles in the coated layer dispersed into a liquid phase and formed a barrier layer to impede the movement of the liquid phase, preventing the pore-filling process and increasing the open porosity of the ceramic specimens. Flexural strengths at room temperature were tested, indicating that increases in the sintering temperature of the specimens without coated fused silica powders had little effect on flexural strength. However, the flexural strength of the specimens with coated fused silica powders increased with increases in sintering temperature. The improvement in flexural strength was related to the reinforcement by sintering necks between particles and the improvement in the strength of the coated fused silica powder.