Eggshell-membrane-templated synthesis of hierarchically-ordered NiO–Ce0.8Gd0.2O1.9 composite powders and their electrochemical performances as SOFC anodes

Abstract Hierarchically-ordered NiO-Ce 0.8 Gd 0.2 O 1.9 (GDC) composite anode powders were synthesized using eggshell membranes as biotemplates. The morphology of the as-synthesized powders depended on the kind of Ni precursor and the use of EDTA as a chelating agent. Hierarchically-ordered anode powders were obtained from Ni chloride and Ni acetate precursors with EDTA. The Ni–GDC anode synthesized from Ni chloride precursor with EDTA exhibited the lowest polarization resistance at 800 °C and an activation energy of 0.01 Ω cm 2 and 0.74 eV, respectively, in humidified H 2 . In accordance with the polarization resistance results, the 0.5-mm thick GDC electrolyte-supported single cell with the Ni–GDC anode synthesized from Ni chloride precursor with EDTA showed a maximum power density of 0.34 W cm −2 at 800 °C with humidified H 2 fuel.