Comparison of the chemical corrosion resistance of magnesia-based refractories by stainless steelmaking slags under vacuum conditions
Source abstract
Abstract
Abstract This study evaluates commercially available magnesia–chromite, magnesia–carbon and magnesia–doloma bricks for their use in a Vacuum Oxygen Decarburisation ladle. The corrosion behaviour of these bricks by stainless steelmaking slags is, therefore, investigated through crucible tests in a vacuum induction furnace at elevated temperatures (1650 and 1750 °C) and low oxygen partial pressures (5.3 and 3.0×10 −11 atm). The results reveal that magnesia–carbon bricks are severely corroded due to the high dissolution of MgO, while magnesia–chromite and magnesia–doloma refractories exhibit an excellent corrosion resistance. The MgO enrichment in the slag is believed to be the reason of the low wear rate of the MgO–doloma refractories. Rebonded and direct-bonded MgO–chromite refractories show similar corrosion resistance against the slags because of the ‘secondary chromite inactivation’. Decreasing the slag basicity enhances the dissolution of MgO into the slag, thereby increasing the corrosion of the magnesia-based refractories.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Metallurgical Processes and Thermodynamics · Materials Engineering and Processing · Advanced ceramic materials synthesis
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (19)
Show source-provided references
1. Formation of hexavalent chromium by reaction between slag and magnesite-chrome refractory10.1007/s11663-998-0117-8 ↗
2. Development of a chromite free VOD ladle refractory lining
3. Behaviour of magnesia–carbon refractories in vacuum–oxygen decarburisation ladle linings10.1179/030192303225003971 ↗
4. Degradation mechanisms of magnesia–chromite refractories by high-alumina stainless steel slags under vacuum conditions10.1016/j.jeurceramsoc.2005.12.025 ↗
5. Degradation mechanisms of magnesia–carbon refractories by high-alumina stainless steel slags under vacuum10.1016/j.ceramint.2006.03.009 ↗
6. The influence of ZnO in fayalite slag on the degradation of magnesia–chromite refractories during secondary Cu smelting10.1016/j.jeurceramsoc.2015.03.013 ↗
7. Degradation of MgO–C refractories by MnO-rich stainless steel slags10.1016/j.ceramint.2008.12.007 ↗
8. Degradation mechanisms of magnesia–chromite refractories in vacumm-oxygen decarburisation ladles during production of stainless steel10.1179/030192300677525 ↗
9. Laboratory set-up to study refractories in VOD process conditions
10. Marangoni flows and corrosion of refractory walls10.1098/rsta.1998.0206 ↗
11. Use of phase diagrams in studies of refractories corrosion10.1179/095066000101528304 ↗
12. A study of slag-infiltrated magnesia–chromite refractories using hybrid microwave heating10.1016/S0955-2219(00)00343-5 ↗
13. Interaction of Al2O3-rich slag with MgO–C refractories during VOD refining—MgO and spinel layer formation at the slag/refractory interface10.1016/j.jeurceramsoc.2008.07.063 ↗
14. In situ observation of the direct and indirect dissolution of MgO particles in CaO–Al2O3–SiO2-based slags10.1016/j.jeurceramsoc.2006.05.107 ↗
15. Melt corrosion of oxide and oxide–carbon refractories10.1179/095066099101528234 ↗
16. Penetration and corrosion of magnesia grain by silicate slags10.1179/096797800681036 ↗
17. Magnesia-graphite refractories for BOF converters
18. Interfacial reaction between refractory materials and metallurgical slags containing fluoride10.1002/srin.201000157 ↗
19. P.T.Jones. Degradation Mechanisms of Basic Refractory Materials During the Secondary Refining of Stainless Steel in VOD Ladles (Ph.D. thesis), Faculteit Ingenieurswetenschappen – Dept. MTM, Leuven, 2000, Chapter 5.