Synthesis and biodegradation evaluation of nano-Si and nano-Si/TiO2 coatings on biodegradable Mg–Ca alloy in simulated body fluid

Abstract In the present study, nano-Si and nano-Si/TiO 2 composite coatings have been successfully synthesized on the surface of Mg–1 wt%Ca alloy by the physical vapor deposition (PVD) method. The surface morphology and compositions of the coated specimens were characterized by X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FTIR), transmission electron microscopy (TEM), scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS). The results show the formation of thin and compact coating layers which homogeneously cover the surface of Mg alloy. Some micro-pores and micro-cracks were observed in the Si and Si/TiO 2 films. It was also found that the Si and TiO 2 nanoparticle had a spherical morphology with an average particle size of 30–40 nm and 70–80 nm, respectively. Electrochemical studies revealed that nano-Si/TiO 2 coating offers a significant reduction in the corrosion rate (0.57 mm/year) compared to the Si coated (0.91 mm/year) and the uncoated alloys (6.21 mm/year) in simulated body fluid (SBF). Hydrogen evolution studies showed a lower degradation rate of nano-Si/TiO 2 (1.57 ml/cm 2 /day) than that of nano-Si coated alloy (2.22 ml/cm 2 /day). Immersion test showed that the nano-Si/TiO 2 coating presented a greater nucleation site of hydroxyapatite (HA) than the uncoated sample. Thus nano-Si/TiO 2 composite coating prepared by PVD on the Mg–Ca alloy is more appropriate for biomedical applications.