Water vapor corrosion resistance and failure mechanism of SiCf/SiC composites completely coated with plasma sprayed tri-layer EBCs
Source abstract
Abstract
Abstract In this work, the corrosion behaviors of as-plasma sprayed Yb2SiO5 and LaMgAl11O19 coatings under an environment with a volumetric ratio of 90% H2O-10% O2 were investigated at 1300 °C. The results showed that Yb2SiO5 and LaMgAl11O19 coatings had good water vapor corrosion resistance. Therefore, Si/Yb2SiO5/LaMgAl11O19 tri-layer EBCs were designed and prepared to completely cover the surface of SiCf/SiC by using atmospheric plasma spraying (APS). The water vapor corrosion behaviors of SiCf/SiC with and without EBCs at 1300 °C were investigated. The results showed that tri-layer coating can provide better corrosion resistance for SiCf/SiC at a high-temperature steam environment at 1300 °C. By comparing the water vapor corrosion behaviors of single-layer coatings and the tri-layer EBCs under same corrosion environment, it was found that the thermal mismatch stress and the formation of TGO is the main causes of tri-layer coating failure.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Advanced ceramic materials synthesis · High-Temperature Coating Behaviors · Metal and Thin Film Mechanics
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (40)
Show source-provided references
1. Rare earth silicate environmental barrier coatings for SiC/SiC composites and Si3N4 ceramics10.1016/j.jeurceramsoc.2004.12.013 ↗
2. Silicon nitride for high-temperature applications10.1111/j.1551-2916.2010.03839.x ↗
3. Property evolutions of Si/mixed Yb2Si2O7 and Yb2SiO5 environmental barrier coatings completely wrapping up SiCf/SiC composites under 1300 °C water vapor corrosion10.1016/j.ceramint.2021.04.246 ↗
4. Development of oxide-based High temperature environmental barrier coatings for ceramic matrix composites via the slurry process10.1016/j.jeurceramsoc.2020.10.012 ↗
5. Phase and microstructure evolution in plasma sprayed Yb2Si2O7 coatings10.1016/j.jeurceramsoc.2018.11.018 ↗
6. A review on environmental barrier coatings: history, current state of the art and future developments10.1016/j.jeurceramsoc.2020.10.057 ↗
7. Upper temperature limit of environmental barrier coatings based on mullite and BSAS10.1111/j.1151-2916.2003.tb03466.x ↗
8. Development of oxide-based EBC for silicon nitride10.1111/j.1744-7402.2004.tb00187.x ↗
9. Thermal properties of rare-earth monosilicates for EBC on Si-based ceramic composites10.1111/jace.13982 ↗
10. Thermal shock behavior of mixed ytterbium disilicates and ytterbium monosilicates composite environmental barrier coatings10.1016/j.surfcoat.2018.08.041 ↗
11. Thermal expansion of rare-earth pyrosilicates10.1111/jace.12388 ↗
12. Effect of processing on high-velocity water vapor recession behavior of Yb-silicate environmental barrier coatings10.1016/j.jeurceramsoc.2018.11.048 ↗
13. Towards multifunctional thermal environmental barrier coatings (TEBCs) based on rare-earth pyrosilicate solid-solution ceramics10.1016/j.scriptamat.2018.05.032 ↗
14. Mechanisms of ytterbium monosilicate/mullite/silicon coating failure during thermal cycling in water vapor10.1111/jace.13792 ↗
15. Plasma spray deposition of tri-layer environmental barrier coatings10.1016/j.jeurceramsoc.2014.04.027 ↗
16. Fracture mechanisms of ytterbium monosilicate environmental barrier coatings during cyclic thermal exposure10.1016/j.actamat.2015.10.019 ↗
17. Interface evolution of Si/Mullite/Yb2SiO5 PS-PVD environmental barrier coatings under high temperature10.1016/j.jeurceramsoc.2019.10.062 ↗
18. Water vapor corrosion behavior of Yb2SiO5 environmental barrier coatings prepared by plasma spray-physical vapor deposition10.3390/coatings10040392 ↗
19. Response of ytterbium disilicate–silicon environmental barrier coatings to thermal cycling in water vapor10.1016/j.actamat.2015.12.053 ↗
20. Microstructure evolution and thermomechanical properties of plasma-sprayed Yb2SiO5 coating during thermal aging10.1111/jace.14690 ↗
21. Microstructure, oxidation protection and failure mechanism of Yb2SiO5/LaMgAl11O19 coating deposited on C/SiC composites by atmospheric plasma spraying10.1016/j.corsci.2012.05.020 ↗
22. A new double layer oxidation resistant coating based on Er2SiO5/LaMgAl11O19 deposited on C/SiC composites by atmospheric plasma spraying10.1016/j.surfcoat.2013.01.011 ↗
23. Microstructure and oxidation resistant behavior of Er2Si2O7 and Er2Si2O7/LaMgAl11O19 coatings deposited on Cf/SiC composites by APS at 1723 K10.1016/j.jallcom.2017.03.108 ↗
24. Fabrication and oxidation resistant behavior of plasma sprayed Si/Yb2Si2O7/LaMgAl11O19 coating for Cf/SiC composites at 1673 K10.1016/j.ceramint.2016.09.171 ↗
25. Oxidation and thermal shock resistant properties of Si/Yb2SiO5/NdMgAl11O19 coating deposited on Cf/SiC composites10.1016/j.matdes.2016.12.022 ↗
26. Thermal properties of oxides with magnetoplumbite structure for advanced thermal barrier coatings10.1016/j.surfcoat.2007.09.048 ↗
27. Failure of the plasma-sprayed coating of lanthanum hexaluminate10.1016/j.jeurceramsoc.2008.01.023 ↗
28. Thermal shock resistance of tri‐layer Yb2SiO5/Yb2Si2O7/Si coating for SiC and SiC‐matrix composites10.1111/jace.15713 ↗
29. Water vapour corrosion of rare earth monosilicates for environmental barrier coating application10.1016/j.ceramint.2017.02.123 ↗
30. Thermochemical stability and microstructural evolution of Yb2Si2O7 in high-velocity high-temperature water vapor10.1016/j.jeurceramsoc.2020.05.071 ↗
31. High temperature corrosion of (Er0.25Tm0.25Yb0.25Lu0.25)2Si2O7 environmental barrier coating material subjected to water vapor and molten calcium–magnesium–aluminosilicate (CMAS)10.1016/j.corsci.2020.108881 ↗
32. Thermal cycling behaviors of the plasma sprayed thermal barrier coatings of hexaluminates with magnetoplumbite structure10.1016/j.jeurceramsoc.2010.01.013 ↗
33. Alumina volatility in water vapor at elevated temperatures10.1111/j.1551-2916.2004.01701.x ↗
34. Effect of spraying power on microstructure and property of nanostructured YSZ thermal barrier coatings10.1016/j.jallcom.2017.09.323 ↗
35. Formation of vertical cracks in air plasma sprayed YSZ coatings using unpyrolyzed powder10.1016/j.ceramint.2020.05.320 ↗
36. Mechanism of vertical crack formation in Yb2SiO5 coatings deposited via plasma spray-physical vapor deposition10.1016/j.jmat.2020.01.002 ↗
37. Mechanical properties and microstructure of Yb2SiO5 environmental barrier coatings under isothermal heat treatment10.1016/j.jeurceramsoc.2019.12.057 ↗
38. Residual stresses and their effects on the durability of environmental barrier coatings for SiC ceramics10.1111/j.1551-2916.2005.00640.x ↗
39. Wet oxidation behaviors of Hi-Nicalon fibers10.1016/j.apsusc.2006.02.021 ↗
40. Hafnium silicate formation during oxidation of a permeable silicon + HfO2 powder composite system10.1016/j.actamat.2020.10.019 ↗