The effect of slip casting parameters on the green density of MgAl 2 O 4 spinel

Abstract The aim of this paper was to investigate the effect of slip casting parameters on the green density of MgAl 2 O 4 spinel. In order to obtain samples with suitable mechanical and optical properties, it is necessary to prepare bulk samples with a fine grain size along with a low level of impurity and high density. Slip casting is widely used in the processing of optical ceramics to achieve a body with high green density and low sintering temperature. In the present study, several spinel suspensions with similar solid content but different viscosities and particle sizes (90, 150, 300 and 500 nm) were prepared and shaped into a dense body. Viscosity of suspension depended on dispersant content, such that the addition of dispersant firstly caused viscosity to decrease, but it was increased by further dispersant addition, irrespective of the suspension particle size. The green density range of samples was 36–67% of the theoretical value. Rheological behaviour and green density measurements showed that powder particles smaller than 90 nm were unsuitable for slip casting because agglomeration of powder particles led to high viscosity and hence, low green density. The optimal particle size for slip casting was found to be 150 nm.