Investigation of substrate bias effects on the reactively sputtered ZrN diffusion barrier films
Source abstract
Abstract
Abstract ZrN diffusion barrier films were prepared by DC reactive magnetron sputtering under different negative substrate bias. The composition, microstructure, resistivity and diffusion barrier properties of ZrN films, with respect to substrate bias, were studied by means of X-ray diffraction, electron probe microanalyzer, Auger electron spectroscopy, and four point probe method. Results showed that the deposition rate and impurity oxygen content of ZrN films were substantially influenced by the resputtering effects due to the ion bombardment on the film surface. The competition between surface energy and strain energy made the preferred orientation of ZrN films change from (1 1 1) to (2 0 0) and then back to highly (1 1 1) preferred orientation as a function of substrate bias. The application of negative substrate bias could effectively decrease the electrical resistivity due to the decrease of impurity oxygen content and the densification of films, resulting from the moderate-energy ion irradiation. The biased ZrN films could successfully be used as a diffusion barrier layer, between Cu and SiO 2 , even up to the high temperature of 800 °C for 30 min.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Metal and Thin Film Mechanics · Semiconductor materials and devices · Copper Interconnects and Reliability
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (35)
Show source-provided references
1. Evaluating the large electromigration resistance of copper interconnects employing a newly developed accelerated life-test method10.1149/1.2056211 ↗
2. Interdiffusions and reactions in Cu/TiN/Ti/Si and Cu/TiN/Ti/SiO2/Si multilayer structures10.1557/JMR.1997.0441 ↗
3. Barrier characteristics of ZrN films deposited by remote plasma-enhanced atomic layer deposition using tetrakis(diethylamino)zirconium precursor10.1143/JJAP.46.4085 ↗
4. Thermal and electrical properties of 5-nm-thick TaN film prepared by atomic layer deposition using a pentakis(ethylmethylamino)tantalum precursor for copper metallization10.1143/JJAP.45.9072 ↗
5. Reaction between Cu and TiSi2 across different barrier layers10.1063/1.104249 ↗
6. Barriers against copper diffusion into silicon and drift through silicon dioxide10.1557/S0883769400047710 ↗
7. Massalski · 1990
8. Approaches to diffusion barrier creation and trench filling for copper interconnection formation10.1007/s00339-005-3259-4 ↗
9. Preparation of single-oriented (111)VN film with low-resistivity and its application as diffusion barrier between Cu and Si10.1143/JJAP.45.215 ↗
10. Application of thin nanocrystalline VN film as a high-performance diffusion barrier between Cu and SiO210.1116/1.1800471 ↗
11. Diffusion barrier properties of ZrN films in the Cu/Si contact systems10.1116/1.591382 ↗
12. Pierson · 1996
13. Application of extremely thin ZrN film as diffusion barrier between Cu and SiOC10.1143/JJAP.47.620 ↗
14. Characteristics of TiN film deposited on stellite using reactive magnetron sputter ion plating10.1557/JMR.1997.0317 ↗
15. X-ray photoelectron spectroscopic studies of the surface of sputter ion plated films10.1002/sia.740060603 ↗
16. Ohring · 1992
17. Systematic study of the evolution of texture and electrical properties of ZrNx thin films by reactive DC magnetron sputtering10.1016/S0040-6090(03)01191-X ↗
18. Analysis of r.f.-sputtered TiB2 hard coatings by means of X-ray diffractometry and Auger electron spectroscopy10.1016/0921-5093(91)90626-X ↗
19. Reactive-sputter-deposited TiN films on glass substrates10.1016/0040-6090(91)90225-M ↗
20. Effects of strain energy on the preferred orientation of TiN thin films10.1063/1.355297 ↗
21. Growth of thin films with preferential crystallographic orientation by ion bombardment during deposition10.1016/S0257-8972(94)80014-6 ↗
22. Marinov · Thin Solid Films · 1977 · 46 · 526710.1016/0040-6090(77)90182-1 ↗
23. Effects of substrate bias on nanocrystal-(Ti,Al)Nx/amorphous-SiNy composite films10.1557/JMR.2003.0275 ↗
24. Klug · 1974
25. Microstructure and physical properties of polycrystalline metastable Ti0.5Al0.5N alloys grown by D.C. magnetron sputter deposition10.1016/0040-6090(87)90169-6 ↗
26. Influence of deposition conditions on the morphology of sputtered W–C–(Co) films10.1016/0040-6090(92)90467-P ↗
27. Effect of ion bombardment during deposition on thick metal and ceramic deposits10.1116/1.1312733 ↗
28. Ohring · 1992
29. Effects of substrate bias and nitrogen flow ratio on the resistivity, density, stoichiometry, and crystal structure of reactively sputtered ZrNx thin films10.1116/1.1776182 ↗
30. Effect of substrate bias on the structure and properties of ion-plated ZrN on Si and stainless steel substrates10.1016/S0254-0584(01)00494-1 ↗
31. The effect of density and microstructure on the performance of TiN barrier films in Cu metallization10.1063/1.363620 ↗
32. Effect of density on the diffusion barrier property of TiNx films between Cu and Si10.1016/j.matchemphys.2004.02.001 ↗
33. Suppression of Cu agglomeration in the Cu/Ta/Si structure by capping layer10.1016/S1468-6996(03)00067-6 ↗
34. Failure mechanism of amorphous and crystalline Ta–N films in the Cu/Ta-N/Ta/SiO2 structure10.1149/1.1803836 ↗
35. Effect of ion bombardment during chemical vapor deposition of TiN films10.1149/1.1393594 ↗