Mechanical and elastic properties of new silicon nitride ceramics produced by cold isostatic pressing and free sintering
Source abstract
Abstract
The mechanical and elastic properties of new silicon nitride fabricated by cold isostatic pressing and free sintering are considered. Young׳s modulus, Poisson׳s ratio and shear modulus of investigated ceramic were determined. An indentation technique for measuring the indentation modulus was developed. The flexural strength, the compressive strength and the fracture toughness were investigated. Young׳s modulus of the obtained material was 240 GPa by resonance and 214 GPa by mechanical tests. The microhardness was 1380 HV0.5 and 970 HK2.5. Obtained silicon nitride ceramic is one of a candidate material for a wide range of structural applications due to its high density (2.94 g/cm3) and low open porosity (0.1%)
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Advanced ceramic materials synthesis · Metal and Thin Film Mechanics · Advanced materials and composites
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (23)
Show source-provided references
1. Temperature-dependence of young modulus and internal-friction in alumina, silicon-nitride, and partially stabilized zirconia ceramics10.1111/j.1151-2916.1984.tb09612.x ↗
2. Structural and electrical properties of silicon nitride ceramic10.3329/diujst.v7i1.9648 ↗
3. Munz · 1999 · 298
4. Effect of dewaxing procedures of cold isostatically pressed silicon nitride ceramics on its microstructure and fracture strength10.1163/156855203322448309 ↗
5. Cold isostatic pressing–normal pressure sintering behavior of amorphous nano-sized silicon nitride powders10.4028/www.scientific.net/AMR.454.17 ↗
6. Brito · 2003 · 142
7. Investigation of the structure of Si3N4-based ceramic with Al2O3 and Y2O3 additives
8. A new improved technique for determining hardness and elastic modulus using load and sensing indentation experiments10.1557/JMR.1992.1564 ↗
9. Effect and measurement of the machine compliance in the macro range of instrumented indentation test10.1016/j.measurement.2009.09.009 ↗
10. C. Ullner, HARDMEKO 2004 hardness measurements theory and application in laboratories and industries 11–12 November, Washington, D.C., USA, critical points in ISO 14577 part 2 and 3 considering the uncertainty in measurement, 2004.
11. Review relationships between processing, microstructure and properties of dense and reaction-bonded silicon nitride10.1007/BF01161167 ↗
12. 〈http://www.azom.com/article.aspx?ArticleID=77〉.
13. Peng · 2004
14. Silicon nitride ceramics for product and process innovations10.4028/www.scientific.net/AST.65.70 ↗
15. Dense and near-net-shape fabrication of Si3N4 ceramics10.1016/j.msea.2008.09.015 ↗
16. Effect of rare-earth oxides on properties of silicon nitride obtained by normal sintering and sinter-HIP10.1016/S1002-0721(12)60201-4 ↗
17. On the microhardness of silicon nitride and sialon ceramics10.1016/0955-2219(90)90021-7 ↗
18. On the Vickers indentation fracture toughness test10.1111/j.1551-2916.2006.01482.x ↗
19. Fischer-Cripps · 2000 · 243
20. Niihara · J. Mater. Sci. Lett. · 1982 · 1 · 1310.1007/BF00724706 ↗
21. The influence of the graphene additive on mechanical properties and wear of hot-pressed Si3N4 matrix composites10.1016/j.jeurceramsoc.2014.08.004 ↗
22. The effect of fabrication parameters on the mechanical properties of sintered reaction bonded porous Si3N4 ceramics10.1016/j.jeurceramsoc.2014.06.018 ↗
23. A simple method for determining elastic-modulus-to hardness ratios using Knoop indentation measurements10.1111/j.1151-2916.1982.tb10357.x ↗