Comparative evaluation investigation of slag corrosion on Al2O3 and MgO-Al2O3 refractories via experiments and thermodynamic simulations
Source abstract
Abstract
Abstract Al 2 O 3 - and MgO-based refractories are widely used in the steel industry as lining materials for many metallurgical reactors. Due to their direct contact with slag and steel, they suffer corrosion and degradation, especially in the slag-line position, which limits their service performance. The purpose of this article is to obtain a better understanding of the corrosion behavior of the two refractories with different compositions of virtual steelmaking slags (wt%CaO/wt%SiO 2 = 3.0–7.0, Al 2 O 3 : 18–35 wt%) using laboratory experiments and FactSage thermodynamic modeling. Pure Al 2 O 3 and MgO-Al 2 O 3 crucibles were adopted to simulate the two refractories, respectively, during the experiment. The results show that the degree of corrosion of both crucibles increases with an increase in slag basicity and a decrease in Al 2 O 3 content in the slag. The Al 2 O 3 crucible is more susceptible to corrosion than the MgO-Al 2 O 3 crucible, which is attributed to the effect of the slag penetrating through the Al 2 O 3 crucible matrix and substituting part of its matrix. For the MgO-Al 2 O 3 crucible, there was no obvious slag substitution, but a transition layer was found in the contact region between the crucible and the slag. The Al 2 O 3 in the crucible matrix reacts with slag to produce calcium alumina (CaAl 12 O 19 , CaAl 4 O 7 ) and other complex oxides, while the MgO particles at the MgO-Al 2 O 3 crucible-slag interface were only surrounded by liquid slag without an obvious chemical reaction between them. The mechanism of corrosion was studied by experiments combined with thermodynamic calculations and with the establishment of a new corrosion model. This study is expected to provide a guide for the design of related refractories and slags in industrial applications.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Metallurgical Processes and Thermodynamics · Materials Engineering and Processing · Corrosion Behavior and Inhibition
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (28)
Show source-provided references
1. Study on foaming behavior of molten slag during smelting reduction with iron bath
2. Solid state chemistry of alumina-chromia-magnesia and related refractories10.1007/BF00626504 ↗
3. FactSage thermodynamic database for steelmaking refractory research
4. Microstructural evolution of magnesia-based castables containing microsilica10.1016/j.ceramint.2012.03.070 ↗
5. Dissolution kinetics of alumina into mold fluxes for continuous steel casting10.2355/isijinternational.45.1856 ↗
6. Dissolution rate of Al2O3 into molten CaO-SiO2-Al2O3 slags10.2355/isijinternational.42.852 ↗
7. Dissolution of alumina in mold fluxes10.1007/s11663-997-0094-3 ↗
8. Diffusional dissolution of alumina in various steelmaking slags10.2355/isijinternational.44.229 ↗
9. C. Tse, S.H. Lee, S. Sridhar, A.W. Cramb In-situ observations of clean steel phenomenon, in: Proceedings of the 83rd Steelmaking Conference, ISS, Pittsburgh, USA, 2000, pp. 219–229.
10. Reactions between MgO-C refractory, molten slag and metal10.2355/isijinternational.40.Suppl_S101 ↗
11. Dissolution behaviour of MgO based refractories in CaO–Al2O3–SiO2 slag, Ironmak10.1179/1743281215Y.0000000003 ↗
12. Melt corrosion of oxide and oxide–carbon refractories10.1179/095066099101528234 ↗
13. Effects of additives and temperature on the dissolution rate and diffusivity of MgO in CaO–Al2O3 slags under forced convection10.2355/isijinternational.46.1554 ↗
14. Corrosion behavior of MgO–C refractory in ferromanganese slags10.2355/isijinternational.52.62 ↗
15. Dissolution rate and mechanism of solid MgO particles in synthetic ladle slags10.1016/j.jnoncrysol.2012.02.014 ↗
16. In situ observation of the direct and indirect dissolution of MgO particles in CaO–Al2O3–SiO2-based slags10.1016/j.jeurceramsoc.2006.05.107 ↗
17. Degradation mechanisms of magnesia-carbon refractories by high-alumina stainless steel slags under vacuum10.1016/j.ceramint.2006.03.009 ↗
18. Corrosion of magnesia–chrome brick in molten MgO–Al2O3–SiO2–CaO–FetO slag10.1016/j.matchemphys.2008.02.001 ↗
19. Corrosion of spinel clinker by CaO–Al2O3–SiO2 ladle slag10.1016/S0955-2219(01)00509-X ↗
20. Basic slag attack of spinel-containing refractory castables10.1016/j.ceramint.2011.02.007 ↗
21. Effect of spinel content on slag attack resistance of high alumina refractory castables10.1016/j.jeurceramsoc.2007.04.007 ↗
22. Corrosion behavior of slags containing TiO2 to Al2O3 ceramic cup during blast furnace ironmaking process
23. Improvement of resistance of MgO-based refractory to slag penetration by in situ spinel formation10.1007/s11663-014-0277-7 ↗
24. Improvement of resistance to slag penetration in magnesia-based refractory with colloidal alumina addition II by means of a proper particle size distribution of MgO10.1007/s11663-016-0649-2 ↗
25. Influence of grain phase on slag corrosion of low-cement castable refractories10.1111/j.1151-2916.2001.tb00672.x ↗
26. The development of a thermodynamic model for Al2O3–MgO refractory castable corrosion by secondary metallurgy steel ladle slags10.1016/j.ceramint.2008.04.002 ↗
27. Slag attack evaluation of in situ spinel-containing refractory castables via experimental tests and thermodynamic simulations10.1016/j.ceramint.2011.09.033 ↗
28. Melt corrosion of oxide and oxide–carbon refractories10.1179/095066099101528234 ↗