Synthesis and ceramic conversion of a novel processible polyboronsilazane precursor to SiBCN ceramic

Abstract Polyboronsilazane (PBSZ) precursors for SiBCN ceramics were prepared by using 9-borabicyclo-[1,3,3] nonane (9-BBN) and copolysilazanes (CPSZ) as starting materials, involving the hydroboration reaction between vinyl groups of PSZ and B H groups of 9-BBN under mild conditions. The as-synthesized PBSZ was obtained as a soluble liquid, which was characterized by FT IR and NMR. The polymer-to-ceramic conversion of PBSZ at a ceramic yield of 62.2–79.9% was investigated by means of FT IR and TGA. The crystallization behavior and microstructures of PBSZ-derived SiBCN ceramics were studied by XRD, SEM and HRTEM. The SiBCN ceramic began to crystallize at 1600 °C. Further heating at 1800 °C induced partial crystallization to give mixed XRD patterns for SiC, Si 3 N 4 , and BN(C). It is observed that the introduction of boron improves the thermal stability of SiBCN ceramics, especially under high temperatures of 1600–1800 °C. In addition, the introduction of boron significantly improves the ceramic density while inhibits the SiC crystallization.