Interfacial microstructure and mechanical properties of porous-Si3N4 ceramic and TiAl alloy joints vacuum brazed with AgCu filler
Source abstract
Abstract
Abstract Porous Si 3 N 4 ceramic was firstly joined to TiAl alloy using an AgCu filler alloy. The effects of brazing temperature and holding time on the interfacial microstructure and mechanical properties of porous-Si 3 N 4 /AgCu/TiAl joints were studied. The typical interfacial microstructure of joints brazed at 880 °C for 15 min was TiAl/AlCu 2 Ti/Ag-Cu eutectic/penetration layer (Ti 5 Si 3 +TiN, Si 3 N 4 , Ag (s, s), Cu (s, s))/porous-Si 3 N 4 . The penetration layer was formed firstly in the brazing process. With increasing brazing temperature and time, the thickness of the penetration layer increased. A large amount of element Ti was consumed in the penetration layer which suppressed the formation and growth of other intermetallic compounds. The penetration layer led the fracture to propagate in the porous Si 3 N 4 ceramic substrate. The maximum shear strength was ~13.56 MPa.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Advanced ceramic materials synthesis · Intermetallics and Advanced Alloy Properties · MXene and MAX Phase Materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (47)
Show source-provided references
1. Silicon nitride and related materials10.1111/j.1151-2916.2000.tb01182.x ↗
2. Relationships between processing, microstructure and properties of dense and reaction-bonded silicon nitride10.1007/BF01161167 ↗
3. Si3N4 and Si2N2O for high performance radomes10.1016/0025-5416(85)90236-8 ↗
4. Fabrication and properties of porous Si3N4–SiO2 ceramics with dense surface and gradient pore distribution10.1016/j.ceramint.2013.09.068 ↗
5. Fabrication and properties of porous silicon nitride wave-transparent ceramics via gel-casting and pressureless sintering10.1016/j.msea.2016.03.116 ↗
6. Fabrication of porous anisotropic silicon nitride by using partial sinter-forging technique10.1016/S0921-5093(01)01907-4 ↗
7. Mechanical and dielectric properties of porous Si2N2O–Si3N4 in situ composites10.1016/j.ceramint.2008.10.021 ↗
8. Mechanical and dielectric properties of porous Si3N4–SiO2 composite ceramics10.1016/j.msea.2008.09.066 ↗
9. Dielectric and mechanical properties of porous Si3N4 ceramics prepared via low temperature sintering10.1016/j.ceramint.2008.09.010 ↗
10. Development of a TiAl turbocharger for passenger vehicles10.1016/S0921-5093(01)01584-2 ↗
11. Development and evaluation of TiAl sheet structures for hypersonic applications10.1016/j.msea.2007.02.020 ↗
12. Effect of cyclic heat treatment parameters on the grain refinement of Ti–48Al–2Cr–2Nb alloy10.1016/j.matchar.2009.03.008 ↗
13. Microstructural changes and estimated strengthening contributions in a gamma alloy Ti–45Al–5Nb pack-rolled sheet10.1016/j.intermet.2009.05.018 ↗
14. Microstructure and mechanical strength of diffusiono-bonded silicon nitride-molybdenum joints10.1016/S0955-2219(99)00027-8 ↗
15. Interfacial microstructure and mechanical characterization of silicon nitride/nickel-base superalloy joints by partial transient liquid phase bonding10.1016/j.ceramint.2015.09.115 ↗
16. Processing, microstructure and mechanical properties of vacuum-brazed Al2O3/Ti6Al4V joints10.1016/j.msea.2011.12.042 ↗
17. The brazing of Si3N4 with Ni-Cr-Si alloys10.1016/0955-2219(95)00015-M ↗
18. Microstructural and mechanical evaluation of a Cu-based active braze alloy to join silicon nitride ceramics10.1016/j.jeurceramsoc.2010.07.022 ↗
19. Microstructural and mechanical characterization of the Si3N4/Si3N4 joint brazed using Au–Ni–V filler alloys10.1016/j.jeurceramsoc.2009.08.015 ↗
20. Interfacial microstructure of the Si3N4/Si3N4 joint brazed with Cu–Pd–Ti filler alloy10.1016/j.jeurceramsoc.2005.11.001 ↗
21. Improvements of the Si3N4 brazed joints with intermetallics10.1016/j.msea.2005.09.096 ↗
22. Formation of interfacial microstructure in brazing of Si3N4 with Ti-activated Ag-Cu filler alloys10.1016/0956-716X(95)00127-H ↗
23. Characterization of the Si3N4/Si3N4 joints fabricated using particles modified braze10.1016/j.msea.2014.08.023 ↗
24. Titanium metallization of Si3N4 ceramics by molten salt reaction: coating microstructure and brazing property10.1016/S0040-6090(02)00950-1 ↗
25. Brazing of Si3N4 ceramic to copper10.1016/S0924-0136(97)00427-5 ↗
26. Brazing silicon nitride to an iron-based intermetallic using a copper interlayer10.1016/j.ceramint.2003.10.011 ↗
27. Metal to ceramic joining via a metallic interlayer bonding technique10.1016/j.jmatprotec.2003.10.005 ↗
28. Stress intensity factors and crack initiation directions for ceramic/metal joint10.1016/S0167-8442(98)00041-X ↗
29. Properties and fractography of Si3N4/TiN ceramic joined to steel with active single layer and double layer braze filler alloys10.1016/j.actamat.2004.06.016 ↗
30. Strain energy release in ceramic-to-metal joints with patterned interlayers10.1016/j.scriptamat.2003.09.055 ↗
31. Distribution and chemistry of phases developed in the brazing of silicon nitride to molybdenum10.1016/S0955-2219(98)00259-3 ↗
32. Nanostructure of wetting triple line in a Ag–Cu–Ti/Si3N4 reactive system10.1016/S1359-6454(98)00375-9 ↗
33. Interfacial microstructure and joining properties of TiAl/Si3N4 brazed joints10.1016/j.msea.2011.05.079 ↗
34. Microstructure evolution and mechanical properties of ZrO2/TiAl joints vacuum brazed by Ag–Cu filler metal10.1016/j.msea.2015.05.059 ↗
35. Effect of holding time on microstructure and mechanical properties of ZrO2/TiAl joints brazed by Ag–Cu filler metal10.1016/j.matdes.2015.08.020 ↗
36. Microstructure and mechanical properties of Al2O3 ceramic and TiAl alloy joints brazed with Ag–Cu–Ti filler metal10.1016/j.ceramint.2016.01.078 ↗
37. Microstructure and mechanical properties of Al2O3 ceramic and Ti6Al4V alloy joint brazed with inactive Ag–Cu and Ag–Cu+B10.1016/j.jeurceramsoc.2016.02.033 ↗
38. Microstructure and strength of the SiC/TiAl joint brazed with Ag-Cu-Ti filler metal10.1023/A:1006773412999 ↗
39. Microstructural evolution and mechanical properties of the joint of TiAl alloys and C/SiC composites vacuum brazed with Ag–Cu filler metal10.1016/j.matchar.2011.05.007 ↗
40. Brazing mechanism and infiltration strengthening of CC composites to TiAl alloys joint10.1016/j.scriptamat.2010.06.035 ↗
41. Microstructure and mechanical properties of silicon nitride ceramics with controlled porosity10.1111/j.1151-2916.2002.tb00305.x ↗
42. Microstructure and mechanical properties of three porous Si3N4 ceramics fabricated by different techniques10.1016/j.msea.2012.03.114 ↗
43. Interfacial microstructure of induction brazed joints of TiAl-based intermetallics to steel 35CrMo with AgCuNiLi filler10.1016/j.msea.2005.08.009 ↗
44. Pelton · 1983
45. Formation of interfacial microstructure in brazing of Si3N4 with Ti-activated Ag-Cu filler alloys10.1016/0956-716X(95)00127-H ↗
46. A dissolution model of base metal in liquid brazing filler metal during high temperature brazing10.1016/j.scriptamat.2003.12.032 ↗
47. Thermal expansion of metal–ceramic composites: a three-dimensional analysis10.1016/S0921-5093(98)00698-4 ↗