Application of BaO–CaO–Al2O3–B2O3–SiO2 glass–ceramic seals in large size planar IT-SOFC

Abstract BaO–CaO–Al 2 O 3 –B 2 O 3 –SiO 2 (BCAS) glass–ceramics can be used as sealant for large size planar anode-supported solid oxide fuel cells (SOFCs). BCAS glass–ceramics after heat treatment for different times were characterized by means of thermal dilatometer, X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results show that the coefficients of thermal expansion (CTE) of BCAS glass–ceramics are 11.4×10 −6 K −1 , 11.3×10 −6 K −1 and 11.2×10 −6 K −1 after heated at 750 °C for 0 h, 50 h, and 100 h, respectively. The CTE of BCAS matches that of YSZ, Ni–YSZ and the interconnection of SOFC. Needle-like barium silicate, barium calcium silicate and hexacelsian are crystallized in the BCAS glass after heat-treatment for above 50 h at 750 °C. The glass–ceramics green tape prepared by aqueous tape casting can be directly applied in sealing the cell of SOFCs with 10 cm×10 cm. The open circuit voltage (OCV) of the cell keeps 1.19 V after running for 280 h at 750 °C and thermal cycling 10 times from 750 °C to room temperature. The maximum power density is 0.42 W/cm 2 using pure H 2 as fuel and air as oxidation gas. SEM images show no cracks or pores exist in the interface of BCAS glass–ceramics and the cell.