Dissolution behavior of a novel Al 2 O 3 -SiC-SiO 2 -C composite refractory in blast furnace slag
Source abstract
Abstract
Abstract Al2O3-SiC-SiO2-C composite refractories are interesting potential blast furnace hearth lining materials that feature several advantageous properties. In this study, the corrosion resistance of a novel Al2O3-SiC-SiO2-C composite refractory to blast furnace slag was investigated by adopting a rotating immersion method (25 r/min) at 1450–1550 °C and comparing it against a conventional corundum-based refractory at 1550 °C as a benchmark. The results showed that the apparent activation energy of Al2O3-SiC-SiO2-C composite refractory over the dissolution process in the slag is 150.4 kJ/mol. Dissolution of the Al2O3 and 3Al2O3·2SiO2 phases appeared to be the main cause of Al2O3-SiC-SiO2-C composite refractory corrosion. High-melting-point compounds in the slag layer formed a protective layer which mitigated the corrosion. The novel Al2O3-SiC-SiO2-C composite refractory is better suited to blast furnace hearth lining than the conventional corundum-based refractory, because the carbon phase and SiC phase in the material are not readily wetted by the blast furnace slag and therefore are more resistant to slag penetration. Higher melting point phases also may crystallize on the hot face of the hearth lining due to the high thermal conductivity of the Al2O3-SiC-SiO2-C composite refractory, promoting a more stable protective layer.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Advanced ceramic materials synthesis · Metallurgical Processes and Thermodynamics · Recycling and utilization of industrial and municipal waste in materials production
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (32)
Show source-provided references
1. Design and operation control for long campaign life of blast furnaces10.1016/S1006-706X(13)60156-9 ↗
2. Recent progress on long service life design of Chinese blast furnace hearth10.2355/isijinternational.52.1713 ↗
3. Pore structure, permeability, and alkali attack resistance of Al2O3-C refractories10.1007/s11661-014-2217-1 ↗
4. Effect of Al4SiC4 on the Al2O3-SiC-SiO2-C refractory castables performance10.1016/j.ceramint.2012.01.027 ↗
5. Carbon containing castables: current status and future prospects10.1179/096797801125000410 ↗
6. High temperature mechanical characterisation of an alumina refractory concrete for blast furnace main trough: Part I. General context10.1016/j.jeurceramsoc.2008.04.031 ↗
7. High-temperature mechanical characterisation of an alumina refractory concrete for blast furnace main trough: Part II. Material behavior10.1016/j.jeurceramsoc.2008.04.027 ↗
8. Slag corrosion of MgO-C refractories during secondary steel refining10.1179/1743281213Y.0000000110 ↗
9. Oxidation behavior and kinetics of Al2O3-SiC-SiO2-C composite in air10.1016/j.ceramint.2015.03.307 ↗
10. Comparison of oxidation behaviors of novel carbon composite brick with traditional carbon brick10.1016/j.ceramint.2015.02.133 ↗
11. High-temperature active/passive oxidation and bubble formation of CVD SiC in O2 and CO2 atmospheres10.1016/S0955-2219(02)00139-5 ↗
12. Experimental investigation of passive/active oxidation behavior of SiC based ceramic thermal protection materials exposed to high enthalpy plasma10.1016/j.jeurceramsoc.2012.09.002 ↗
13. Effect of electromagnetic field on slag corrosion resistance of low carbon MgO-C refractories10.1016/j.ceramint.2011.10.049 ↗
14. An efficient MgAl2O4 spinel additive for improved slag erosion and penetration resistance of high-Al2O3 and MgO-C refractories10.1016/S0272-8842(01)00086-4 ↗
15. Investigation of slag-refractory interactions for the Ruhrstahl Heraeus (RH) vacuum degassing process in steelmaking10.1016/j.jeurceramsoc.2012.01.005 ↗
16. Chemical wear of Al2O3-MgO-C bricks by air and basic slag10.1016/j.jeurceramsoc.2014.11.024 ↗
17. Slag conditioning effects on MgO-C refractory corrosion performance10.1016/j.ceramint.2013.03.001 ↗
18. Slag attack evaluation of in situ spinel-containing refractory castables via experimental tests and thermodynamic simulations10.1016/j.ceramint.2011.09.033 ↗
19. Corrosion of magnesium aluminate spinel-rich refractories by sulphur-containing slag10.1016/j.jeurceramsoc.2014.11.031 ↗
20. Thermodynamic evaluation of spinel containing refractory castables corrosion by secondary metallurgy slag10.1016/j.ceramint.2010.11.043 ↗
21. Effect of spinel content on slag attack resistance of high alumina refractory castables10.1016/j.jeurceramsoc.2007.04.007 ↗
22. Effects of transition metals on the kinetics of slag-refractory reactions10.1007/s11663-001-0004-z ↗
23. Investigation of in-situ chemical reactions of Al2O3-SiC-SiO2-C refractory and its interactions with slag10.2355/isijinternational.44.785 ↗
24. Study on the slag corrosion resistance of unfired Al2O3-SiC/β-Sialon/Ti(C, N)-C refractories10.1016/j.ceramint.2013.07.047 ↗
25. Post mortem study of Al2O3/SiC/C/MgAl2O4 ceramic lining used in torpedo cars10.1016/j.ceramint.2004.09.016 ↗
26. Influence of additives on slag resistance of Al2O3-SiO2-SiC-C refractory bond phases under reducing atmosphere10.1111/j.1151-2916.1998.tb02754.x ↗
27. Thermodynamic evaluation of SiC oxidation in Al2O3-MgAl2O4-SiC-SiO2-C refractory castables10.1016/j.ceramint.2010.03.021 ↗
28. Solid-liquid interactions: the key to microstructural evolution in ceramics10.1016/j.jeurceramsoc.2007.12.010 ↗
29. BF slag resistance of β-Si3Al3O3N5 material derived from Al salt cake10.1016/j.jeurceramsoc.2014.11.002 ↗
30. Viscosities behavior of CaO-SiO2-MgO-Al2O3 slag with low mass ratio of CaO to SiO2 and wide range of A12O3 content10.1016/S1006-706X(11)60015-0 ↗
31. Preparation and oxidation of bauxite-based β-Sialon-bonded SiC composite10.1016/j.materresbull.2006.02.027 ↗
32. Spinelisation and properties of Al2O3–MgAl2O4–C refractory: effect of MgO and Al2O3 reactants10.1016/j.ceramint.2009.12.011 ↗