Carbothermal reduction synthesis of TiB2 ultrafine powders

Abstract Submicrometric TiB 2 powders were synthesized by carbothermal reduction process using titanium dioxide, boron carbide and carbon black as the starting materials. The influence of different amount of boron carbide (22.0–26.8 wt%), calcination temperature (1400–1900 °C) and holding time (15–90 min) on the composition and microstructure of the product was investigated. The resultant powders were characterized by X-ray diffraction (XRD) and scanning electron microscope (SEM). Results showed that hexagonal impurity-free TiB 2 crystalline powders with the grain size below 1.0 μm could be successfully prepared at 1600 °C for 30 min in Ar atmosphere when the amount of boron carbide was 25.3 wt%. The increase in temperature contributed to reaction completion and grain growth, but the abnormal grain growth and oversintering took place above 1800 °C.