Electrolyte materials for solid oxide fuel cells derived from metal complexes: Gadolinia-doped ceria

Abstract Gadolinia doped ceria (GDC) powders with different gadolinium contents were successfully prepared by the thermal decomposition of ceria complexes. All the calcined powder samples were found to be ceria-based solid-solutions having a fluorite-type structure. The powders were cold-isostatically pressed and sintered in air at 1500 °C for 5 h to attain a sintered density of about 90% of its theoretical value. The electrical conductivity of the GDC pellets in air was studied as a function of temperature in the 225–700 °C range, by using two-probe electrochemical impedance spectroscopy measurements. The highest total conductivity ( σ 600 °C = 0.025 S/cm) was found for the Ce 0.85 Gd 0.15 O 1.925 composition.