Low-temperature sintering of coarse alumina powder compact with sufficient mechanical strength

Abstract Coarse alumina powder compacts doped with various amounts of titania and copper oxide were pressurelessly sintered from 900 °C to 1600 °C. Their phase assemblages and microstructural evolution, as well as their properties, were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), differential scanning calorimetry/thermogravimetric (DSC/TG) analysis, and three-point bending and wetting test. The role of TiO 2 and CuO during the sintering is discussed in detail. The experimental results show that the liquid phase from the copper oxide appeared at approximately 1200 °C, so the solid-state reaction between alumina and titania took place at a lower temperature. Such solid state-reaction sintering had a strong impact on the grain growth and greatly promoted the densification of the alumina compact. In addition, the liquid phase inhibited the abnormal grain growth and microcracking. As a result, the coarse alumina powder compacts doped with 5 wt% TiO 2 –CuO were fully densified and exhibited sufficient flexural strength (342±21 MPa) when sintered at a temperature of 1450 °C for 2 h.