Fabrication and plasma resistance properties of transparent YAG ceramics
Source abstract
Abstract
Abstract High quality transparent yttrium aluminum garnet (YAG) ceramics with an average grain size of about 12 μm have been fabricated by a solid state reactive sintering method. Plasma resistance property of the fabricated YAG ceramics was studied and compared with that of the Y 2 O 3 ceramics, silicate glass and quartz. The YAG ceramics showed an excellent plasma resistance as well as Y 2 O 3 ceramics. After etching in F-plasma for 6 h, the eroded depth of YAG ceramics was about 100 nm. The plasma resistance of YAG ceramics was far better than that of silicate glass and quartz.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Plasma Diagnostics and Applications · Optical Coatings and Gratings · Thin-Film Transistor Technologies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (6)
Show source-provided references
1. Plasma etching: principles mechanisms, application to micro- and nano-technologies10.1016/S0169-4332(00)00328-7 ↗
2. Dense yttrium oxide film prepared by aerosol deposition process at room temperature10.2109/jcersj.114.272 ↗
3. Plasma-resistant dense yttrium oxide film prepared by aerosol deposition process10.1111/j.1551-2916.2007.01738.x ↗
4. Y. Kobayashi, M. Ichishima, Y. Yokoyama, Plasma resistant member, U.S. Patent 7,090,932, 2006.
5. M. Fujita, K. Morita, Plasma-resistant member for semiconductor manufacturing apparatus and method for manufacturing the same, U.S. Patent 6,838,405, 2005.
6. High etch selectivity for plasma etching SiO2 with AlN and Al2O3 masks10.1016/j.mee.2007.12.037 ↗