Effects of the structure of CeCu catalysts on the catalytic combustion of toluene in air

Abstract CeCu composite oxide catalysts were prepared by a hard-template method (CeCu-HT) and a complex method (CeCu-CA). The prepared CeCu composite oxide catalysts were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), and Brunauer–Emmett–Teller (BET) analyses. The catalytic properties of the prepared CeCu composite oxide catalysts were also investigated by the catalytic combustion of toluene in air. XRD results showed that the synthesized CeCu composite oxide catalysts had different phase components and crystallinities but similar CeO 2 CuO solid solution phases. Low-angle XRD, TEM, and BET results indicated that the prepared CeCu-HT catalyst had a developed ordered mesoporous structure and a large specific surface area of 206.1 m 2 g −1 . Toluene catalytic combustion results indicated that the CeCu-HT catalyst had higher toluene catalytic combustion activity in air than the CeCu-CA catalyst. The minimum reaction temperature at which toluene conversion exceeded 90% for toluene catalytic combustion on the CeCu-HT catalyst was 225 °C. The toluene catalytic combustion conversion on the CeCu-HT catalyst at 240 °C exceeded 99.3% with decreased toluene concentration in air to below 70 ppm. On the other hand, the toluene catalytic combustion conversion on the CeCu-CA catalyst was only 92% even when the reaction temperature reached 280 °C. The differences between the toluene catalytic combustion performances of the CeCu composite oxide catalysts prepared by different methods can be attributed to their discrepant compositions and structures.